NORYL PPX™ Resin PPX640F - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL PPX™ 640F resin is a 40% glass reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This injection moldable grade is NSF 61 certified and exhibits high elongation and stiffness along with temperature performance, impact resistance, hydrolytic and dimensional stability. NORYL PPX640F resin is an excellent candidate for copper and brass replacement in water management applications such as water filtration systems, boiler systems, and heat exchangers.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.3 [-]

Show Supplier Material materials with Relative density of 1.3 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

6.4 %

Show Supplier Material materials with Elongation of 6.4 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

8.31 GPa

Show Supplier Material materials with Flexural modulus of 8.31 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

150 MPa

Show Supplier Material materials with Flexural strength of 150 MPa

ASTM D 790 | brk, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

106 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 106 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

96 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 96 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

576 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 576 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

16 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 16 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

95 MPa

Show Supplier Material materials with Tensile strength of 95 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.08E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.08E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.3E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

158 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 158 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

146 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 146 °C

ASTM D 648 | 3.2mm, unannealed

Vicat softening temperature

163 °C

Show Supplier Material materials with Vicat softening temperature of 163 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221228- -

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

1.3 g/10min

Show Supplier Material materials with Melt mass-flow rate of 1.3 g/10min

ASTM D 1238 | 260°C/5.0 kgf

Shrinkage

23.0 °C

0.17 %

Show Supplier Material materials with Shrinkage of 0.17 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.27 %

Show Supplier Material materials with Shrinkage, transverse of 0.27 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Water Treatment/Filtration, Photovoltaic Components

Availability

Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Good Stiffness, Low Warpage, Food Contact Acceptable, Structural

Processing methods

Drying Time (Cumulative): 8hrs
Drying Temperature: 65 to 75.0°C
Middle - Zone 2 Temperature: 250 to 290.0°C
Maximum Moisture Content: 0.02%
Drying Time: 2 to 4.0hrs
Shot to Cylinder Size: 30 to 70.0%
Vent Depth: 0.051 to 0.076mm
Rear - Zone 1 Temperature: 245 to 290.0°C
Back Pressure: 0.3 to 0.7MPa
Nozzle Temperature: 260 to 305.0°C
Front - Zone 3 Temperature: 255 to 300.0°C
Melt Temperature: 260 to 305.0°C
Mold Temperature: 40 to 65.0°C
Screw Speed: 20 to 100.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.