NORYL GTX™ Resin GTX626 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 626 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This blow moldable and extrudable grade exhibits high heat resistance and excellent chemical resistance. NORYL GTX626 resin may be an excellent candidate for exterior automotive applications such as wheel covers and wheel trim.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.09 [-]

Show Supplier Material materials with Relative density of 1.09 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

83 %

Show Supplier Material materials with Elongation of 83 %

ASTM D 638 | brk, Type I, 50 mm/min

Flexural modulus

23.0 °C

2.27 GPa

Show Supplier Material materials with Flexural modulus of 2.27 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

95 MPa

Show Supplier Material materials with Flexural strength of 95 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

336 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 336 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

336 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 336 J/m

ASTM D 256

Instrumented Impact, at Peak

23.0 °C

31 J

Show Supplier Material materials with Instrumented Impact, at Peak of 31 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

62 MPa

Show Supplier Material materials with Tensile strength of 62 MPa

ASTM D 638 | yld, Type I, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

179 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 179 °C

ASTM D 648 | 6.4 mm, unannealed

Flammability

UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=220758- -

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.3 %

Show Supplier Material materials with Shrinkage of 1.3 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Exterior, Heavy Vehicles

Availability

Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, High Heat Resistance, Low Warpage

Processing methods

Barrel - Zone 1 Temperature: 270 to 280.0°C
Die Temperature: 275 to 290.0°C
Melt Temperature (Parison): 275 to 290.0°C
Adapter - Zone 5 Temperature: 275 to 290.0°C
Drying Time: 4hrs
Mold Temperature: 80°C
Barrel - Zone 4 Temperature: 270 to 280.0°C
Barrel - Zone 2 Temperature: 270 to 280.0°C
Drying Time (Cumulative): 16hrs
Head - Zone 7 - Bottom Temperature: 275 to 290.0°C
Barrel - Zone 3 Temperature: 270 to 280.0°C
Head - Zone 6 - Top Temperature: 275 to 290.0°C
Drying Temperature: 80°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.