ULTEM™ Resin 1010TC - Asia

Want to keep this datasheet? Save it now in your required format

Description

ULTEMTM 1010TC resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217C, with UL94 V0 and 5VA ratings offering high heat resistance and infrared transmission.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ISO 1183

Limiting oxygen index

23.0 °C

44 %

Show Supplier Material materials with Limiting oxygen index of 44 %

Moisture absorption

23.0 °C

0.7 %

Show Supplier Material materials with Moisture absorption of 0.7 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.27 [-]

Show Supplier Material materials with Relative density of 1.27 [-]

ASTM D 792 |

Water absorption

23.0 °C

1.25 %

Show Supplier Material materials with Water absorption of 1.25 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Elastic modulus of 3.2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 5 mm/min

Flexural modulus

23.0 °C

3.3 GPa

Show Supplier Material materials with Flexural modulus of 3.3 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

160 MPa

Show Supplier Material materials with Flexural strength of 160 MPa

ISO 178 | yield, 2 mm/min

Hardness, Rockwell M

23.0 °C

109 [-]

Show Supplier Material materials with Hardness, Rockwell M of 109 [-]

ASTM D 785 |

Impact strength, Charpy notched

23.0 °C

3 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 3 kJ/m²

ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

32 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 32 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

1335 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1335 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

33 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 33 J

ASTM D 3763 | 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

105 MPa

Show Supplier Material materials with Tensile strength of 105 MPa

ISO 527 | yield, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

207 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 207 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

193 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 193 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

170 °C

Show Supplier Material materials with Relative temperature index, electrical of 170 °C

UL 746B

Relative temperature index, mechanical impact

170 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 170 °C

UL 746B

Relative temperature index, mechanical strength

170 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 170 °C

UL 746B

Thermal conductivity

23.0 °C

0.22 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K)

ASTM C177

Vicat softening temperature

212 °C

Show Supplier Material materials with Vicat softening temperature of 212 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥3mm UL 94 <br> NBS Smoke Density, Flaming, Ds 4 min: 2- ASTM E 662 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100221357- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

Dielectric strength

23.0 °C

32.6 kV/mm

Show Supplier Material materials with Dielectric strength of 32.6 kV/mm

ASTM D 149 | in air, 1.6 mm

Dissipation factor

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor of 2.5E-3 [-]

ASTM D 150 | 2450 MHz

Dissipation factor, 1kHz

23.0 °C

1.3E-3 [-]

Show Supplier Material materials with Dissipation factor, 1kHz of 1.3E-3 [-]

ASTM D 150

High Amp Arc Ignition

23.0 °C

3 mm

Show Supplier Material materials with High Amp Arc Ignition of 3 mm

≥, UL 746A | PLC 3

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

3 mm

Show Supplier Material materials with Hot-Wire Ignition of 3 mm

≥, UL 746A | PLC 1

Volume resistivity

23.0 °C

1.00E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

17.8 g/10min

Show Supplier Material materials with Melt mass-flow rate of 17.8 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Melt volume-flow rate

25 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 25 cm³/10min

ISO 1133 | MVR at 220°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Data Transfer, Electronic Components, Medical Device, Wireless Communications

Availability

Asia

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Attenuation Control, Infrared Transparent, Easy Flow, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, General Purpose, High Heat Resistance, Good dimensional stability, Flame Retardant

Processing methods

Drying Time (Cumulative): 24hrs
Back Pressure: 0.3 to 0.7MPa
Maximum Moisture Content: 0.02%
Middle - Zone 2 Temperature: 340 to 400.0°C
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 350 to 400.0°C
Mold Temperature: 135 to 165.0°C
Front - Zone 3 Temperature: 345 to 400.0°C
Rear - Zone 1 Temperature: 330 to 400.0°C
Drying Time: 4 to 6.0hrs
Screw Speed: 40 to 70.0rpm
Nozzle Temperature: 345 to 400.0°C
Drying Temperature: 150°C
Shot to Cylinder Size: 40 to 60.0%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.