LNP™ THERMOCOMP™ AM Compound DC004XXAR1 - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP™ THERMOCOMP™ AM, grade name DC004XXAR1, is a compound based on PC resin containing 20% carbon fiber for Large Format Additive manufacturing (LFAM) applications needing higher stiffness vs glass fiber. PC based compounds deliver higher strength, higher temperature performance and higher throughput compared to ABS and PPE, as well as excellent ductility and smooth surface finish

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.27 [-]

Show Supplier Material materials with Relative density of 1.27 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

1.6 %

Show Supplier Material materials with Elongation of 1.6 %

Modified ASTM D638 | 5mm/min

Flexural strength

23.0 °C

66 MPa

Show Supplier Material materials with Flexural strength of 66 MPa

Modified ASTM D790 | 5mm/min

Tensile strength

23.0 °C

124 MPa

Show Supplier Material materials with Tensile strength of 124 MPa

Modified ASTM D638 | 5mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

144 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 144 °C

ASTM D 648 | 3.2mm, annealed,

Technological properties

Property
Application areas

PANELS FOR AUTOMOBILES

Availability

Americas

Processing methods

Extruder L/D: 24-
Drying Temperature: 120°C
Drying Time: 4hrs
Maximum Moisture Content: 0.02%
Barrel - Zone 1 Temperature: 250 to 280.0°C
Barrel - Zone 2 Temperature: 260 to 290.0°C
Barrel - Zone 3 Temperature: 260 to 290.0°C
Barrel - Zone 4 Temperature: 260 to 290.0°C
Nozzle Temperature: 260 to 290.0°C
Melt Temperature: 260 to 290.0°C
Bed Temperature: 100 to 120.0°C
Extruder Pressure: <11MPa

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.