General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³ | ISO 1183 |
Limiting oxygen index | 23.0 °C | 45 % Show Supplier Material materials with Limiting oxygen index of 45 % | |
Moisture absorption | 23.0 °C | 0.65 % Show Supplier Material materials with Moisture absorption of 0.65 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.3 [-] Show Supplier Material materials with Relative density of 1.3 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 1.75 % Show Supplier Material materials with Water absorption of 1.75 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Supplier Material materials with Elastic modulus of 3.1 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 8.4 % Show Supplier Material materials with Elongation of 8.4 % | ISO 527 | yield, 5 mm/min | ||
Flexural modulus | 23.0 °C | 3.1 GPa Show Supplier Material materials with Flexural modulus of 3.1 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 123 MPa Show Supplier Material materials with Flexural strength of 123 MPa | ISO 178 | break, 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 138 MPa Show Supplier Material materials with Hardness, Ball Indentation of 138 MPa | ISO 2039-1 | H358/30 | ||
Impact strength, Izod notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | 80*10*4, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m | ASTM D 256 | ||
Impact strength, Izod unnotched | 23.0 °C | 196 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 196 kJ/m² | ISO 180/1U | 80*10*4, 23°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 33 J Show Supplier Material materials with Instrumented Impact, Total Energy of 33 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 95 MPa Show Supplier Material materials with Tensile strength of 95 MPa | ISO 527 | yield, 5 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | Passes | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature | 228 - 237 °C Show Supplier Material materials with Heat deflection temperature of 228 - 237 °C | ||||
Heat deflection temperature, 0.45 MPa | 237 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 237 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 228 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 228 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 160 °C Show Supplier Material materials with Relative temperature index, electrical of 160 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 160 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 160 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.22 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K) | ASTM E 1530 | | ||
Vicat softening temperature | 240 °C Show Supplier Material materials with Vicat softening temperature of 240 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=257957- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Supplier Material materials with Comparative tracking index of 3 V | UL 746A | (UL) {PLC} |
Dielectric constant, 100Hz | 23.0 °C | 3.38 [-] Show Supplier Material materials with Dielectric constant, 100Hz of 3.38 [-] | ASTM D 150 |
Dielectric strength | 23.0 °C | 14 kV/mm Show Supplier Material materials with Dielectric strength of 14 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Dissipation factor, 100Hz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 8E-3 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 7E-3 [-] | IEC 60250 |
Dissipation factor, 1kHz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 1E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.02 [-] | IEC 60250 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm | ≥, UL 746A | PLC 4 |
Hot-Wire Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm | ≥, UL 746A | PLC 2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 15.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 15.5 g/10min | ASTM D 1238 | 367°C/6.6 kgf | |
Melt volume-flow rate | 8 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Non-LED Lighting | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 150°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |