ULTEM™ Resin CRS5301 - Americas

Want to keep this datasheet? Save it now in your required format

Description

30% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.51 [-]

Show Supplier Material materials with Relative density of 1.51 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

8.96 GPa

Show Supplier Material materials with Elastic modulus of 8.96 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

8.96 GPa

Show Supplier Material materials with Flexural modulus of 8.96 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

234 MPa

Show Supplier Material materials with Flexural strength of 234 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

112 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 112 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

112 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 112 J/m

ASTM D 256

Tensile strength

23.0 °C

165 MPa

Show Supplier Material materials with Tensile strength of 165 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

221 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 221 °C

ASTM D 648 | 6.4 mm, unannealed

Relative temperature index, electrical

105 °C

Show Supplier Material materials with Relative temperature index, electrical of 105 °C

UL 746B

Relative temperature index, mechanical impact

105 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C

UL 746B

Relative temperature index, mechanical strength

105 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C

UL 746B

Flammability

UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221120- -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

4 V

Show Supplier Material materials with Comparative tracking index of 4 V

UL 746A | (UL) {PLC}

High Amp Arc Ignition

23.0 °C

1.5 mm

Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm

≥, UL 746A | PLC 3

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

3 mm

Show Supplier Material materials with Hot-Wire Ignition of 3 mm

≥, UL 746A | PLC 2

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

1.8 g/10min

Show Supplier Material materials with Melt mass-flow rate of 1.8 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Shrinkage

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components

Availability

Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Enhanced Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant

Processing methods

Drying Time (Cumulative): 24hrs
Back Pressure: 0.3 to 0.7MPa
Nozzle Temperature: 360 to 380.0°C
Drying Time: 4 to 6.0hrs
Vent Depth: 0.025 to 0.076mm
Front - Zone 3 Temperature: 365 to 390.0°C
Shot to Cylinder Size: 40 to 60.0%
Maximum Moisture Content: 0.02%
Melt Temperature: 365 to 390.0°C
Middle - Zone 2 Temperature: 355 to 375.0°C
Drying Temperature: 150°C
Mold Temperature: 135 to 165.0°C
Rear - Zone 1 Temperature: 345 to 365.0°C
Screw Speed: 40 to 70.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.