ULTEM™ Resin 2312EPR - Asia

Want to keep this datasheet? Save it now in your required format

Description

30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Electronics

Display Devices

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.48 g/cm³ Show Supplier Material materials with Density of 1.48 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.5 % Show Supplier Material materials with Moisture absorption of 0.5 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.48 [-] Show Supplier Material materials with Relative density of 1.48 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.9 % Show Supplier Material materials with Water absorption of 0.9 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	5.3 GPa Show Supplier Material materials with Elastic modulus of 5.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2 % Show Supplier Material materials with Elongation of 2 %	ISO 527 \| yield, 5 mm/min
Flexural modulus	23.0 °C	5.5 GPa Show Supplier Material materials with Flexural modulus of 5.5 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	145 MPa Show Supplier Material materials with Flexural strength of 145 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, -30°C
Impact strength, Charpy unnotched	23.0 °C	25 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 25 kJ/m²	ISO 179/1eU \| Unnotch Edgew 80104 sp=62mm, -30°C
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	39 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 39 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	25 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 25 kJ/m²	ISO 180/1U \| 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	330 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 330 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, Total Energy	23.0 °C	15 J Show Supplier Material materials with Instrumented Impact, Total Energy of 15 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	80 MPa Show Supplier Material materials with Tensile strength of 80 MPa	ISO 527 \| yield, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Ball Pressure Test		Passes	IEC 60695-10-2 \| 125°C +/- 2°C
Coefficient of thermal expansion	23.0 °C	3.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.2E-5 1/K	ISO 11359-2 \| 23°C to 150°C
Coefficient of thermal expansion, transverse	23.0 °C	3.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.5E-5 1/K	ISO 11359-2 \| 23°C to 150°C
Heat deflection temperature		192 - 204 °C Show Supplier Material materials with Heat deflection temperature of 192 - 204 °C
Heat deflection temperature, 0.45 MPa		204 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 204 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		192 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 192 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Relative temperature index, electrical		105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C	UL 746B
Relative temperature index, mechanical impact		105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C	UL 746B
Relative temperature index, mechanical strength		105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C	UL 746B
Thermal conductivity	23.0 °C	0.32 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.32 W/(m·K)	ISO 8302
Vicat softening temperature		211 °C Show Supplier Material materials with Vicat softening temperature of 211 °C	ISO 306 \| Rate B/50
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221101- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.4mm UL 94

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	4 V Show Supplier Material materials with Comparative tracking index of 4 V	UL 746A \| (UL) {PLC}
High Amp Arc Ignition	23.0 °C	0.4 mm Show Supplier Material materials with High Amp Arc Ignition of 0.4 mm	≥, UL 746A \| PLC 4
High Volt Arc Track Rate	23.0 °C	4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm	≥, UL 746A \| PLC 1

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		13.7 g/10min Show Supplier Material materials with Melt mass-flow rate of 13.7 g/10min	ASTM D 1238 \| 337°C/6.6 kgf
Melt volume-flow rate		14 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 14 cm³/10min	ISO 1133 \| MVR at 360°C/5.0 kg
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Wiring Devices
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 150°C Drying Time: 4 to 6.0hrs Drying Time (Cumulative): 24hrs Maximum Moisture Content: 0.02% Melt Temperature: 350 to 400.0°C Nozzle Temperature: 345 to 400.0°C Front - Zone 3 Temperature: 345 to 400.0°C Middle - Zone 2 Temperature: 340 to 400.0°C Rear - Zone 1 Temperature: 330 to 400.0°C Mold Temperature: 135 to 165.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Shot to Cylinder Size: 40 to 60.0% Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.