NORYL GTX™ Resin GTX964 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 964 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance and high melt flow for optimized processability. NORYL GTX964 resin is impact modified and designed for automotive exterior thin wall, large parts such as body panels.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.08 g/cm³

Show Supplier Material materials with Density of 1.08 g/cm³

ISO 1183

Moisture absorption

23.0 °C

1.19 %

Show Supplier Material materials with Moisture absorption of 1.19 %

ISO 62 | (23°C / 50% RH)

Water absorption

23.0 °C

3.5 %

Show Supplier Material materials with Water absorption of 3.5 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2 GPa

Show Supplier Material materials with Elastic modulus of 2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

4 %

Show Supplier Material materials with Elongation of 4 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

1.8 GPa

Show Supplier Material materials with Flexural modulus of 1.8 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

70 MPa

Show Supplier Material materials with Flexural strength of 70 MPa

ISO 178 | yield, 2 mm/min

Hardness, Ball Indentation

23.0 °C

80 MPa

Show Supplier Material materials with Hardness, Ball Indentation of 80 MPa

ISO 2039-1 | H358/30

Impact strength, Charpy notched

23.0 °C

45 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 45 kJ/m²

ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm

Impact strength, Izod notched

23.0 °C

20 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 20 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Tensile strength

23.0 °C

45 MPa

Show Supplier Material materials with Tensile strength of 45 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K

ISO 11359-2 | 23°C to 60°C

Coefficient of thermal expansion, transverse

23.0 °C

9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K

ISO 11359-2 | 23°C to 60°C

Heat deflection temperature

175 °C

Show Supplier Material materials with Heat deflection temperature of 175 °C

Heat deflection temperature, 0.45 MPa

175 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 175 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Thermal conductivity

23.0 °C

0.23 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.23 W/(m·K)

ISO 8302

Vicat softening temperature

180 °C

Show Supplier Material materials with Vicat softening temperature of 180 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

7 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 7 cm³/10min

ISO 1133 | MVR at 280°C/2.16 kg

Shrinkage

23.0 °C

1.4 %

Show Supplier Material materials with Shrinkage of 1.4 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Auto Aftermarket

Availability

Europe

Processing methods

Melt Temperature: 290 to 320.0°C
Drying Temperature: 100 to 120.0°C
Drying Time: 2 to 3.0hrs
Rear - Zone 1 Temperature: 260 to 280.0°C
Front - Zone 3 Temperature: 290 to 320.0°C
Middle - Zone 2 Temperature: 280 to 300.0°C
Maximum Moisture Content: 0.07%
Hopper Temperature: 60 to 80.0°C
Nozzle Temperature: 280 to 310.0°C
Mold Temperature: 80 to 120.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.