General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.07 g/cm³ Show Supplier Material materials with Density of 1.07 g/cm³ | ISO 1183 |
Limiting oxygen index | 23.0 °C | 21 % Show Supplier Material materials with Limiting oxygen index of 21 % | |
Moisture absorption | 23.0 °C | 1.2 % Show Supplier Material materials with Moisture absorption of 1.2 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.08 [-] Show Supplier Material materials with Relative density of 1.08 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 3.5 % Show Supplier Material materials with Water absorption of 3.5 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2 GPa Show Supplier Material materials with Elastic modulus of 2 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 50 % Show Supplier Material materials with Elongation of 50 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 1.9 GPa Show Supplier Material materials with Flexural modulus of 1.9 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 75 MPa Show Supplier Material materials with Flexural strength of 75 MPa | ISO 178 | yield, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 75 MPa Show Supplier Material materials with Hardness, Ball Indentation of 75 MPa | ISO 2039-1 | H358/30 |
Impact strength, Charpy notched | 23.0 °C | 55 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 55 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 25 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 280 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 280 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 55 J Show Supplier Material materials with Instrumented Impact, Total Energy of 55 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 45 MPa Show Supplier Material materials with Tensile strength of 45 MPa | ISO 527 | break, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature | 175 °C Show Supplier Material materials with Heat deflection temperature of 175 °C | ||||
Heat deflection temperature, 0.45 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Thermal conductivity | 23.0 °C | 0.24 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.24 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 180 °C Show Supplier Material materials with Vicat softening temperature of 180 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | IEC 60112 | |
Dielectric constant, 1MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.7 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.5 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.5 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 20 kV/mm Show Supplier Material materials with Dielectric strength of 20 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 0.07 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.07 [-] | IEC 60250 | 50/60 Hz |
Volume resistivity | 23.0 °C | 2.20E+13 Ω·cm Show Supplier Material materials with Volume resistivity of 2.20E+13 Ω·cm | IEC 60093 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 12.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 12.5 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Melt volume-flow rate | 12 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Shrinkage | 23.0 °C | 1.4 % Show Supplier Material materials with Shrinkage of 1.4 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 1.1 % Show Supplier Material materials with Shrinkage, transverse of 1.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Exterior, Heavy Vehicles, Head Protection, Enclosures, Electronic Components, Defense, Building Element | |
Availability | Europe | |
Processing methods | Hopper Temperature: 60 to 80.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |