NORYL GTX™ Resin GTX942 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 942 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high melt flow, excellent chemical resistance and paintability. NORYL GTX942 resin was designed for large part / thin wall applications.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.09 g/cm³

Show Supplier Material materials with Density of 1.09 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.52 %

Show Supplier Material materials with Moisture absorption of 0.52 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.09 [-]

Show Supplier Material materials with Relative density of 1.09 [-]

ASTM D 792 |

Water absorption

23.0 °C

1.01 %

Show Supplier Material materials with Water absorption of 1.01 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.58 GPa

Show Supplier Material materials with Elastic modulus of 2.58 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

7.1 %

Show Supplier Material materials with Elongation of 7.1 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.22 GPa

Show Supplier Material materials with Flexural modulus of 2.22 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

88 MPa

Show Supplier Material materials with Flexural strength of 88 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

23 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 23 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

265 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 265 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

46 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 46 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

58 MPa

Show Supplier Material materials with Tensile strength of 58 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1E-4 1/K

ISO 11359-2 | 23°C to 80°C

Coefficient of thermal expansion, transverse

23.0 °C

5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K

ISO 11359-2 | 23°C to 80°C

Heat deflection temperature

154 °C

Show Supplier Material materials with Heat deflection temperature of 154 °C

Heat deflection temperature, 0.45 MPa

154 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 154 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Vicat softening temperature

169 °C

Show Supplier Material materials with Vicat softening temperature of 169 °C

ISO 306 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

18.5 g/10min

Show Supplier Material materials with Melt mass-flow rate of 18.5 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Melt volume-flow rate

17 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

1.13 %

Show Supplier Material materials with Shrinkage of 1.13 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Wireless Communications, Heavy Vehicles, Lawn/Garden, Exterior

Availability

Americas

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Good Stiffness, Low Warpage, High Flow, Good Processability

Processing methods

Rear - Zone 1 Temperature: 260 to 300.0°C
Shot to Cylinder Size: 30 to 50.0%
Minimum Moisture Content: 0.02%
Vent Depth: 0.013 to 0.038mm
Drying Temperature: 95 to 105.0°C
Front - Zone 3 Temperature: 270 to 300.0°C
Drying Time: 3 to 4.0hrs
Middle - Zone 2 Temperature: 265 to 300.0°C
Mold Temperature: 65 to 95.0°C
Screw Speed: 20 to 100.0rpm
Back Pressure: 0.3 to 1.4MPa
Nozzle Temperature: 275 to 300.0°C
Maximum Moisture Content: 0.07%
Drying Time (Cumulative): 8hrs
Melt Temperature: 275 to 300.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.