General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.09 g/cm³ Show Supplier Material materials with Density of 1.09 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.2 % Show Supplier Material materials with Moisture absorption of 1.2 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.1 [-] Show Supplier Material materials with Relative density of 1.1 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 3.5 % Show Supplier Material materials with Water absorption of 3.5 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.1 GPa Show Supplier Material materials with Elastic modulus of 2.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 7.5 % Show Supplier Material materials with Elongation of 7.5 % | ISO 527 | yield, 50 mm/min |
Flexural modulus | 23.0 °C | 2 GPa Show Supplier Material materials with Flexural modulus of 2 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 80 MPa Show Supplier Material materials with Flexural strength of 80 MPa | ISO 178 | yield, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 90 MPa Show Supplier Material materials with Hardness, Ball Indentation of 90 MPa | ISO 2039-1 | H358/30 |
Impact strength, Charpy notched | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 30 kJ/m² | ISO 179/2C | 23°C |
Impact strength, Izod notched | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 120 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 120 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C |
Taber Abrasion | 23.0 °C | 15 mg/1000cy Show Supplier Material materials with Taber Abrasion of 15 mg/1000cy | SABIC method | CS-17, 1 kg |
Tensile strength | 23.0 °C | 55 MPa Show Supplier Material materials with Tensile strength of 55 MPa | ISO 527 | yield, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature | 180 °C Show Supplier Material materials with Heat deflection temperature of 180 °C | ||||
Heat deflection temperature, 0.45 MPa | 180 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 180 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Thermal conductivity | 23.0 °C | 0.23 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.23 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 190 °C Show Supplier Material materials with Vicat softening temperature of 190 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | IEC 60112 | |
Dielectric constant, 1MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.7 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.5 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.5 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 20 kV/mm Show Supplier Material materials with Dielectric strength of 20 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 0.07 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.07 [-] | IEC 60250 | 50/60 Hz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 12 g/10min Show Supplier Material materials with Melt mass-flow rate of 12 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Melt volume-flow rate | 11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Shrinkage | 23.0 °C | 1.5 % Show Supplier Material materials with Shrinkage of 1.5 % | SABIC method | on tensile bar |
Shrinkage, transverse | 23.0 °C | 1.1 % Show Supplier Material materials with Shrinkage, transverse of 1.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Applique, Wheel Cover, Auto Aftermarket, Console, Data Management, Exterior Trim, Heavy Vehicles, Enclosures, Electronic Components | |
Availability | Europe | |
Processing methods | Maximum Moisture Content: 0.07% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |