NORYL GTX™ Resin GTX909 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 909 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high impact performance, high heat resistance, and excellent chemical resistance. NORYL GTX909 resin may be an excellent candidate for various exterior automotive applications such as door handles and wheel covers.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.13 [-]

Show Supplier Material materials with Relative density of 1.13 [-]

ASTM D 792

Water absorption

23.0 °C

0.54 %

Show Supplier Material materials with Water absorption of 0.54 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

9 %

Show Supplier Material materials with Elongation of 9 %

ASTM D 638 | yld, Type I, 50 mm/min

Flexural modulus

23.0 °C

2.37 GPa

Show Supplier Material materials with Flexural modulus of 2.37 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

99 MPa

Show Supplier Material materials with Flexural strength of 99 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

176 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 176 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

106 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 106 J/m

ASTM D 256

Instrumented Impact, at Peak

23.0 °C

40 J

Show Supplier Material materials with Instrumented Impact, at Peak of 40 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

59 MPa

Show Supplier Material materials with Tensile strength of 59 MPa

ASTM D 638 | brk, Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

9.54E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9.54E-5 1/K

ASTM E 831 | -20°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

8.1E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.1E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature, 0.45 MPa

204 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 204 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

125 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C

ASTM D 648 | 6.4 mm, unannealed

Vicat softening temperature

245 °C

Show Supplier Material materials with Vicat softening temperature of 245 °C

ASTM D 1525 | Rate B/50

Electrical

PropertyTemperatureValueComment

Dielectric constant, 1MHz

23.0 °C

2.76 [-]

Show Supplier Material materials with Dielectric constant, 1MHz of 2.76 [-]

ASTM D 150

Dielectric constant, 60Hz

23.0 °C

3.27 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 3.27 [-]

ASTM D 150 | 50/60 Hz

Dielectric strength

23.0 °C

25.5 kV/mm

Show Supplier Material materials with Dielectric strength of 25.5 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor, 1MHz

23.0 °C

0.02 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-]

ASTM D 150 |

Dissipation factor, 50Hz

23.0 °C

0.04 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 0.04 [-]

ASTM D 150 | 50/60 Hz

Sheet resistivity, ROA

23.0 °C

1.70E+16 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 1.70E+16 Ω

ASTM D 257

Volume resistivity

23.0 °C

4.40E+16 Ω·cm

Show Supplier Material materials with Volume resistivity of 4.40E+16 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.3 %

Show Supplier Material materials with Shrinkage of 1.3 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Wheel Cover, Plumbing, Door Handle, Enclosures

Availability

Asia

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Good Tensile Strength, Good Stiffness, Low Warpage, High Impact Resistance

Processing methods

Rear - Zone 1 Temperature: 255 to 295.0°C
Melt Temperature: 270 to 295.0°C
Front - Zone 3 Temperature: 265 to 295.0°C
Mold Temperature: 65 to 95.0°C
Drying Time (Cumulative): 8hrs
Drying Temperature: 95 to 105.0°C
Shot to Cylinder Size: 30 to 50.0%
Nozzle Temperature: 270 to 295.0°C
Minimum Moisture Content: 0.02%
Back Pressure: 0.3 to 1.4MPa
Middle - Zone 2 Temperature: 260 to 295.0°C
Vent Depth: 0.013 to 0.038mm
Drying Time: 3 to 4.0hrs
Maximum Moisture Content: 0.07%
Screw Speed: 20 to 100.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.