NORYL GTX™ Resin GTX6203 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 6203 resin is a 20% talc reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has low co efficient of thermal expansion (CTE), excellent processability, superior dimensional stability, and good surface appearance. NORYL GTX6203 resin is an excellent candidate for automotive exterior body panels.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.24 g/cm³

Show Supplier Material materials with Density of 1.24 g/cm³

ISO 1183

Moisture absorption

23.0 °C

1.1 %

Show Supplier Material materials with Moisture absorption of 1.1 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.25 [-]

Show Supplier Material materials with Relative density of 1.25 [-]

ASTM D 792

Water absorption

23.0 °C

3.2 %

Show Supplier Material materials with Water absorption of 3.2 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.9 GPa

Show Supplier Material materials with Elastic modulus of 4.9 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

10 %

Show Supplier Material materials with Elongation of 10 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

4 GPa

Show Supplier Material materials with Flexural modulus of 4 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

90 MPa

Show Supplier Material materials with Flexural strength of 90 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

60 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m

ASTM D 256

Impact strength, Izod unnotched

23.0 °C

50 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 50 kJ/m²

ISO 180/1U | unnotched 80*10*4, 23°C

Instrumented Impact, Total Energy

23.0 °C

10 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

60 MPa

Show Supplier Material materials with Tensile strength of 60 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

7.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7.5E-5 1/K

ISO 11359-2 | 23°C to 80°C

Coefficient of thermal expansion, transverse

23.0 °C

9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K

ISO 11359-2 | 23°C to 80°C

Heat deflection temperature

190 °C

Show Supplier Material materials with Heat deflection temperature of 190 °C

Heat deflection temperature, 0.45 MPa

190 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 190 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Thermal conductivity

23.0 °C

0.26 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.26 W/(m·K)

ISO 8302

Vicat softening temperature

190 °C

Show Supplier Material materials with Vicat softening temperature of 190 °C

ISO 306 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

20 g/10min

Show Supplier Material materials with Melt mass-flow rate of 20 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Melt volume-flow rate

20 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 20 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage, transverse of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Wheel Cover, Exterior Trim, Engine Cooling System, Enclosures, Auto Aftermarket

Availability

Asia

Features

Hydrolytic Stability, Chemical Resistance, Low Creep Sensitivity, Good Stiffness, Low Warpage, Exceptional Processing, Aesthetics & Visual effects, Structural

Processing methods

Hopper Temperature: 60 to 80.0°C
Mold Temperature: 80 to 100.0°C
Melt Temperature: 280 to 300.0°C
Rear - Zone 1 Temperature: 260 to 280.0°C
Front - Zone 3 Temperature: 280 to 300.0°C
Drying Time: 2 to 3.0hrs
Nozzle Temperature: 270 to 290.0°C
Maximum Moisture Content: 0.07%
Drying Temperature: 100 to 110.0°C
Middle - Zone 2 Temperature: 270 to 290.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.