NORYL™ Resin PX0844 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ PX0844 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade exhibits very low moisture absorption, hydrolytic stability, dimensional stabilty, good foam adhesion, and property retention over a wide temperature range. NORYL PX0844 resin is inherently UL94 HB and is an excellent candidate for automotive interior applications such as instrument panels, audio components, speaker housings, and interior trim. *see NORYL PX0888 resin for higher heat resistance.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Electronics

Display Devices

Automotive

General Automotive Parts

Automotive Exterior

Construction

Packaging

Water Management

Consumer Goods

Domestic Electrical Appliances

Show all

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Water absorption	23.0 °C	0.1 % Show Supplier Material materials with Water absorption of 0.1 %	ASTM D 570 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	40 % Show Supplier Material materials with Elongation of 40 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	65 MPa Show Supplier Material materials with Flexural strength of 65 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Izod notched	23.0 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²	ISO 180/1A \| 80104, -30°C
Tensile strength	23.0 °C	35 MPa Show Supplier Material materials with Tensile strength of 35 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	7.38E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.38E-5 1/K	ASTM E 831 \| 0°C to 100°C
Heat deflection temperature		107 - 122 °C Show Supplier Material materials with Heat deflection temperature of 107 - 122 °C
Heat deflection temperature, 0.45 MPa		122 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 122 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa		107 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 107 °C	ISO 75/Ae \| Edgew 120104 sp=100mm

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Motorcycle, Refrigerator, Photovoltaic Components, Plumbing, Wearables, Wiring Devices, Auto Electrical, Audio, Auto Aftermarket, Data Management, Data Transfer, Document Handling, Drain Pan, Gas/Electric Oven, Heavy Vehicles, Hygiene/Personal Care, Food Transportation, Enclosures, Enclosure/Housing/Cover, Electronic Components
Availability	Europe,Asia,Americas
Processing methods	Vent Depth: 0.038 to 0.051mm Screw Speed: 20 to 100.0rpm Melt Temperature: 275 to 305.0°C Middle - Zone 2 Temperature: 255 to 300.0°C Nozzle Temperature: 275 to 305.0°C Drying Temperature: 105 to 110.0°C Rear - Zone 1 Temperature: 245 to 295.0°C Mold Temperature: 70 to 100.0°C Drying Time: 3 to 4.0hrs Shot to Cylinder Size: 30 to 70.0% Maximum Moisture Content: 0.02% Front - Zone 3 Temperature: 265 to 305.0°C Drying Time (Cumulative): 8hrs Back Pressure: 0.3 to 0.7MPa
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.