NORYL™ Resin PKN4775 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL PKN4775 resin is a non-reinforced, opaque blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high heat, thin wall extrusion and injection moldable grade is an improved version of NORYL PKN4736 resin and exhibits modulus at elevated temperature and good chemical resistance. NORYL PKN4775 resin is an excellent candidate for applications in high performance packaging. *See NORYL PKN4775F resin for FDA food compliant version.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.05 g/cm³

Show Supplier Material materials with Density of 1.05 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.05 %

Show Supplier Material materials with Moisture absorption of 0.05 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.05 [-]

Show Supplier Material materials with Relative density of 1.05 [-]

ASTM D 792

Water absorption

23.0 °C

0.25 %

Show Supplier Material materials with Water absorption of 0.25 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.12 GPa

Show Supplier Material materials with Elastic modulus of 2.12 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

29.3 %

Show Supplier Material materials with Elongation of 29.3 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.16 GPa

Show Supplier Material materials with Flexural modulus of 2.16 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

82 MPa

Show Supplier Material materials with Flexural strength of 82 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

19 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 19 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

268 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 268 J/m

ASTM D 256 | notched, 23°C

Instrumented Impact, Total Energy

23.0 °C

39 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 39 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

47 MPa

Show Supplier Material materials with Tensile strength of 47 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 75°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

9.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9.2E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

9.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9.5E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

122 - 138 °C

Show Supplier Material materials with Heat deflection temperature of 122 - 138 °C

Heat deflection temperature, 0.45 MPa

138 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 138 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

122 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 122 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

144 °C

Show Supplier Material materials with Vicat softening temperature of 144 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

15.3 g/10min

Show Supplier Material materials with Melt mass-flow rate of 15.3 g/10min

ASTM D 1238 | 300°C/5.0 kgf

Melt volume-flow rate

14 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 14 cm³/10min

ISO 1133 | MVR at 300°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Food Container

Availability

Americas

Features

Low Creep Sensitivity, High Heat Resistance, Low Warpage

Processing methods

Maximum Moisture Content: 0%
Die Temperature: 240 to 265.0°C
Drying Temperature: 70 to 80.0°C
Barrel - Zone 4 Temperature: 240 to 265.0°C
Melt Temperature: 265 to 275.0°C
Adapter Temperature: 240 to 265.0°C
Drying Time (Cumulative): 8hrs
Drying Time: 2 to 4.0hrs
Roll Stack Temp - Top: 105 to 120.0°C
Roll Stack Temp - Bottom: 105 to 120.0°C
Barrel - Zone 2 Temperature: 215 to 240.0°C
Barrel - Zone 3 Temperature: 240 to 265.0°C
Roll Stack Temp - Middle: 105 to 120.0°C
Barrel - Zone 1 Temperature: 205 to 225.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.