NORYL™ Resin PKN4752F - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL PKN4752F resin is a non-reinforced, translucent, high heat blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This extrudable and injection moldable grade is FDA food contact compliant and exhibits high heat resistance, dimensional stability, and appears translucent with a yellow tint in the natural color. NORYL PKN4752F resin is an excellent candidate for high performance packaging in food, electronics, and healthcare. *See NORYL PKN4752 resin for NON FDA compliant version.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.08 [-]

Show Supplier Material materials with Relative density of 1.08 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3 GPa

Show Supplier Material materials with Elastic modulus of 3 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

15 %

Show Supplier Material materials with Elongation of 15 %

ASTM D 638 | brk, Type I, 50 mm/min

Flexural modulus

23.0 °C

3.15 GPa

Show Supplier Material materials with Flexural modulus of 3.15 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

144 MPa

Show Supplier Material materials with Flexural strength of 144 MPa

ASTM D 790 | yld, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

32 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 32 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

32 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 32 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

6 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 6 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

73 MPa

Show Supplier Material materials with Tensile strength of 73 MPa

ASTM D 638 | brk, Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6.3E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

5.58E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.58E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

160 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 160 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

151 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 151 °C

ASTM D 648 | 6.4 mm, unannealed

Vicat softening temperature

173 °C

Show Supplier Material materials with Vicat softening temperature of 173 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Availability

Americas

Features

Hydrolytic Stability, Low Creep Sensitivity, High Heat Resistance, Low Warpage, Food Contact Acceptable

Processing methods

Maximum Moisture Content: 0%
Die Temperature: 240 to 265.0°C
Adapter Temperature: 240 to 265.0°C
Roll Stack Temp - Bottom: 105 to 120.0°C
Drying Time: 2 to 4.0hrs
Roll Stack Temp - Middle: 105 to 120.0°C
Roll Stack Temp - Top: 105 to 120.0°C
Barrel - Zone 2 Temperature: 215 to 240.0°C
Melt Temperature: 265 to 275.0°C
Barrel - Zone 1 Temperature: 205 to 225.0°C
Barrel - Zone 4 Temperature: 240 to 265.0°C
Drying Temperature: 70 to 80.0°C
Barrel - Zone 3 Temperature: 240 to 265.0°C
Drying Time (Cumulative): 8hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.