NORYL™ Resin PKN4752 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL PKN4752 resin is a non-reinforced, translucent, high heat blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This extrudable and injection moldable grade exhibits high heat resistance, dimensional stability, and appears translucent with a yellow tint in the natural color. NORYL PKN4752 resin is an excellent candidate for high performance packaging in food, electronics, and healthcare. *See NORYL PKN4752F resin for FDA food compliant version.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Electronics

Semiconductor Devices

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	3 GPa Show Supplier Material materials with Elastic modulus of 3 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	6 % Show Supplier Material materials with Elongation of 6 %	ASTM D 638 \| yld, Type I, 50 mm/min
Flexural modulus	23.0 °C	2.9 GPa Show Supplier Material materials with Flexural modulus of 2.9 GPa	ASTM D 790 \| 2.6 mm/min, 100 mm span
Flexural strength	23.0 °C	144 MPa Show Supplier Material materials with Flexural strength of 144 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	32 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 32 kJ/m²	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	73 MPa Show Supplier Material materials with Tensile strength of 73 MPa	ASTM D 638 \| brk, Type I, 50 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	151 - 160 °C Show Supplier Material materials with Heat deflection temperature of 151 - 160 °C
Heat deflection temperature, 0.45 MPa	160 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 160 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	151 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 151 °C	ASTM D 648 \| 6.4 mm, unannealed
Vicat softening temperature	173 °C Show Supplier Material materials with Vicat softening temperature of 173 °C	ASTM D 1525 \| Rate B/50

Technological properties

Property
Application areas	Bottles, Audio, Additive Semiconductor Materials, Food Container, Electronic Components
Availability	Europe,Asia,Americas
Processing methods	Melt Temperature: 265 to 275.0°C Drying Time (Cumulative): 8hrs Barrel - Zone 1 Temperature: 205 to 225.0°C Barrel - Zone 3 Temperature: 240 to 265.0°C Adapter Temperature: 240 to 265.0°C Die Temperature: 240 to 265.0°C Maximum Moisture Content: 0% Barrel - Zone 4 Temperature: 240 to 265.0°C Roll Stack Temp - Middle: 105 to 120.0°C Barrel - Zone 2 Temperature: 215 to 240.0°C Drying Temperature: 70 to 80.0°C Drying Time: 2 to 4.0hrs Roll Stack Temp - Top: 105 to 120.0°C Roll Stack Temp - Bottom: 105 to 120.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.