NORYL™ Resin PKN4752 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL PKN4752 resin is a non-reinforced, translucent, high heat blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This extrudable and injection moldable grade exhibits high heat resistance, dimensional stability, and appears translucent with a yellow tint in the natural color. NORYL PKN4752 resin is an excellent candidate for high performance packaging in food, electronics, and healthcare. *See NORYL PKN4752F resin for FDA food compliant version.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.1 GPa

Show Supplier Material materials with Elastic modulus of 3.1 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.95 GPa

Show Supplier Material materials with Flexural modulus of 2.95 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

130 MPa

Show Supplier Material materials with Flexural strength of 130 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

3 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 3 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Tensile strength

23.0 °C

86 MPa

Show Supplier Material materials with Tensile strength of 86 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

163 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 163 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

147 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 147 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Vicat softening temperature

174 °C

Show Supplier Material materials with Vicat softening temperature of 174 °C

ISO 306 | Rate A/50

Technological properties

Property
Application areas

Bottles, Audio, Additive Semiconductor Materials, Food Container, Electronic Components

Availability

Europe,Asia,Americas

Features

Hydrolytic Stability, Low Creep Sensitivity, High Heat Resistance, Translucent, Low Warpage

Processing methods

Melt Temperature: 280 to 300.0°C
Hopper Temperature: 50 to 70.0°C
Drying Time: 2 to 4.0hrs
Barrel - Zone 4 Temperature: 250 to 275.0°C
Barrel - Zone 2 Temperature: 225 to 250.0°C
Barrel - Zone 1 Temperature: 215 to 240.0°C
Barrel - Zone 3 Temperature: 250 to 275.0°C
Calibrator Temperature: 60 to 80.0°C
Die Temperature: 250 to 275.0°C
Drying Temperature: 80 to 95.0°C
Adapter Temperature: 250 to 275.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.