NORYL™ Resin IGN320 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ IGN320 resin is a 20% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade exhibits high heat resistance, high modulus, very low moisture absorption, and good dimensional stability. NORYL IGN320 resin is an excellent candidate for automotive applications such as ignition coils where heat and high modulus is required.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.2 [-]

Show Supplier Material materials with Relative density of 1.2 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

6.26 GPa

Show Supplier Material materials with Elastic modulus of 6.26 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

2.4 %

Show Supplier Material materials with Elongation of 2.4 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

5.72 GPa

Show Supplier Material materials with Flexural modulus of 5.72 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

170 MPa

Show Supplier Material materials with Flexural strength of 170 MPa

ASTM D 790 | brk, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

101 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 101 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

101 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 101 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

512 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 512 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

16 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 16 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

108 MPa

Show Supplier Material materials with Tensile strength of 108 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

164 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 164 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

158 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 158 °C

ASTM D 648 | 3.2mm, unannealed

Vicat softening temperature

175 °C

Show Supplier Material materials with Vicat softening temperature of 175 °C

ASTM D 1525 | Rate B/50

Electrical

PropertyTemperatureValueComment

Dielectric strength

23.0 °C

33.9 kV/mm

Show Supplier Material materials with Dielectric strength of 33.9 kV/mm

ASTM D 149 | in oil, 1.6 mm

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

12.8 g/10min

Show Supplier Material materials with Melt mass-flow rate of 12.8 g/10min

ASTM D 1238 | 300°C/5.0 kgf

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage, transverse of 0.2 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Engine Component, EV/HEV Invertor/Convertor, Auto Aftermarket, Sensor, Ignition System

Availability

Americas

Features

Hydrolytic Stability, Low Creep Sensitivity, High Heat Resistance, Good Stiffness, Low Warpage, Structural

Processing methods

Rear - Zone 1 Temperature: 265 to 315.0°C
Back Pressure: 0.3 to 0.7MPa
Melt Temperature: 300 to 325.0°C
Drying Time (Cumulative): 8hrs
Shot to Cylinder Size: 30 to 70.0%
Middle - Zone 2 Temperature: 275 to 320.0°C
Mold Temperature: 80 to 110.0°C
Screw Speed: 20 to 100.0rpm
Drying Temperature: 110 to 120.0°C
Maximum Moisture Content: 0.02%
Drying Time: 3 to 4.0hrs
Nozzle Temperature: 300 to 325.0°C
Front - Zone 3 Temperature: 290 to 325.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.