NORYL™ Resin HNA033 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ HNA033 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade is heat stabilized and impact modified and was designed to withstand high heat autoclave sterilization <350 cycles. In addition, this grade is US FDA and European Food Contact approved, biocompatible (ISO10993 or USP Class VI), RoHS compliant, and it is subject to SABIC’s Healthcare management of change and formulation lock. NORYL HNA033 resin may be an excellent candidate for applications requiring multiple sterilization cycles such as disposable dental xray mouth guards and surgical stapler components.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.08 g/cm³

Show Supplier Material materials with Density of 1.08 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.05 %

Show Supplier Material materials with Moisture absorption of 0.05 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.08 [-]

Show Supplier Material materials with Relative density of 1.08 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.15 %

Show Supplier Material materials with Water absorption of 0.15 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.6 GPa

Show Supplier Material materials with Elastic modulus of 2.6 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

5.2 %

Show Supplier Material materials with Elongation of 5.2 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.6 GPa

Show Supplier Material materials with Flexural modulus of 2.6 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

107 MPa

Show Supplier Material materials with Flexural strength of 107 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

144 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 144 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

47 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 47 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

68 MPa

Show Supplier Material materials with Tensile strength of 68 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.09E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7.09E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.87E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.87E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

141 °C

Show Supplier Material materials with Heat deflection temperature of 141 °C

Heat deflection temperature, 1.80 MPa

141 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 141 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

162 °C

Show Supplier Material materials with Vicat softening temperature of 162 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

8.3 g/10min

Show Supplier Material materials with Melt mass-flow rate of 8.3 g/10min

ASTM D 1238 | 300°C/5.0 kgf

Melt volume-flow rate

8 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min

ISO 1133 | MVR at 300°C/5.0 kg

Shrinkage

23.0 °C

0.7 %

Show Supplier Material materials with Shrinkage of 0.7 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Pharmaceutical Packaging & Drug Delivery, Surgical Devices, Surgical Tray, Animal Testing

Availability

Europe,Asia,Americas

Processing methods

Shot to Cylinder Size: 30 to 70.0%
Mold Temperature: 75 to 105.0°C
Drying Temperature: 105 to 110.0°C
Drying Time (Cumulative): 8hrs
Front - Zone 3 Temperature: 270 to 310.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 20 to 100.0rpm
Melt Temperature: 280 to 310.0°C
Middle - Zone 2 Temperature: 260 to 305.0°C
Rear - Zone 1 Temperature: 250 to 300.0°C
Drying Time: 3 to 4.0hrs
Maximum Moisture Content: 0.02%
Nozzle Temperature: 280 to 310.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.