NORYL™ Resin HN731A - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ HN731A resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade is US FDA and European Food Contact approved, biocompatible (ISO10993 or USP Class VI), RoHS compliant, and It is subject to SABIC’s Healthcare management of change and formulation lock. NORYL HN731A resin exhibits good impact resistance, excellent hydrolytical stability, and chemical resistance. This light weight and colorable material is an excellent candidate for medical device and pharmaceutical applications such as drug-delivery inhalers.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.06 g/cm³

Show Supplier Material materials with Density of 1.06 g/cm³

ISO 1183

Limiting oxygen index

23.0 °C

22 %

Show Supplier Material materials with Limiting oxygen index of 22 %

Moisture absorption

23.0 °C

0.06 %

Show Supplier Material materials with Moisture absorption of 0.06 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.06 [-]

Show Supplier Material materials with Relative density of 1.06 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.23 %

Show Supplier Material materials with Water absorption of 0.23 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.3 GPa

Show Supplier Material materials with Elastic modulus of 2.3 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

30 %

Show Supplier Material materials with Elongation of 30 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.2 GPa

Show Supplier Material materials with Flexural modulus of 2.2 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

75 MPa

Show Supplier Material materials with Flexural strength of 75 MPa

ISO 178 | yield, 2 mm/min

Gardner Impact

23.0 °C

5 J

Show Supplier Material materials with Gardner Impact of 5 J

ASTM D 3029 | -40°C

Hardness, Rockwell R

23.0 °C

119 [-]

Show Supplier Material materials with Hardness, Rockwell R of 119 [-]

ASTM D 785

Impact strength, Charpy notched

23.0 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

213 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 213 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

48 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 48 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

50 MPa

Show Supplier Material materials with Tensile strength of 50 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

115 - 131 °C

Show Supplier Material materials with Heat deflection temperature of 115 - 131 °C

Heat deflection temperature, 0.45 MPa

131 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 131 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

115 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 115 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Relative temperature index, electrical

105 °C

Show Supplier Material materials with Relative temperature index, electrical of 105 °C

UL 746B

Relative temperature index, mechanical impact

90 °C

Show Supplier Material materials with Relative temperature index, mechanical impact of 90 °C

UL 746B

Relative temperature index, mechanical strength

105 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C

UL 746B

Vicat softening temperature

135 °C

Show Supplier Material materials with Vicat softening temperature of 135 °C

ISO 306 | Rate B/50

Flammability

UL Recognized, 94HB Flame Class Rating: 1.47mm UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

3 V

Show Supplier Material materials with Comparative tracking index of 3 V

UL 746A | (UL) {PLC}

Dielectric constant, 60Hz

23.0 °C

2.65 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 2.65 [-]

ASTM D 150 | 50/60 Hz

Dielectric strength

23.0 °C

21.6 kV/mm

Show Supplier Material materials with Dielectric strength of 21.6 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor, 50Hz

23.0 °C

4E-4 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 4E-4 [-]

ASTM D 150 | 50/60 Hz

High Amp Arc Ignition

23.0 °C

0 mm

Show Supplier Material materials with High Amp Arc Ignition of 0 mm

UL 746A | surface {PLC}

High Volt Arc Track Rate

23.0 °C

4 PLC Code

Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code

UL 746A | (PLC)

Hot-Wire Ignition

23.0 °C

2 mm

Show Supplier Material materials with Hot-Wire Ignition of 2 mm

UL 746A | (PLC)

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

9.2 g/10min

Show Supplier Material materials with Melt mass-flow rate of 9.2 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Melt volume-flow rate

8 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min

ISO 1133 | MVR at 280°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage, transverse of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Medical Device, Pharmaceutical Packaging & Drug Delivery, Renal and Blood Handling, Respiratory, Enclosures, Lab Ware and Clinical Diagnostics

Availability

Americas

Processing methods

Drying Time: 3 to 4.0hrs
Maximum Moisture Content: 0.02%
Nozzle Temperature: 280 to 310.0°C
Rear - Zone 1 Temperature: 250 to 300.0°C
Mold Temperature: 75 to 105.0°C
Drying Time (Cumulative): 8hrs
Shot to Cylinder Size: 30 to 70.0%
Back Pressure: 0.3 to 0.7MPa
Front - Zone 3 Temperature: 270 to 310.0°C
Melt Temperature: 280 to 310.0°C
Middle - Zone 2 Temperature: 260 to 305.0°C
Screw Speed: 20 to 100.0rpm
Drying Temperature: 105 to 110.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.