NORYL™ Resin EM7301HF - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ EM7301HF resin is a 10% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade has high flow and improved polyurethane foam adhesion along with creep resistance, dimensional stability, and hydrolytic stability. NORYL EM7301HF resin is an excellent candidate for automotive interior applications such as audio speaker components. This material is available only in black.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.11 [-]

Show Supplier Material materials with Relative density of 1.11 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ASTM D 638 | brk, Type I, 50 mm/min

Flexural modulus

23.0 °C

3.6 GPa

Show Supplier Material materials with Flexural modulus of 3.6 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

104 MPa

Show Supplier Material materials with Flexural strength of 104 MPa

ASTM D 790 | yld, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

80 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 80 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

80 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m

ASTM D 256

Tensile strength

23.0 °C

71 MPa

Show Supplier Material materials with Tensile strength of 71 MPa

ASTM D 638 | yld, Type I, 50 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

112 °C

Show Supplier Material materials with Heat deflection temperature of 112 °C

Heat deflection temperature, 1.80 MPa

112 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 112 °C

ASTM D 648 | 6.4 mm, unannealed

Technological properties

Property
Availability

Asia

Processing methods

Melt Temperature: 260 to 290.0°C
Drying Temperature: 100 to 110.0°C
Mold Temperature: 70 to 90.0°C
Drying Time (Cumulative): 8hrs
Drying Time: 2 to 4.0hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.