FLEX NORYL™ Resin WCD895 - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCD895 resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting UL 1581 VW-1 requirement and 80C end use temperature rating as defined by UL 1581. FLEX NORYL WCD895 resin is intended for evaluation wire and cable jacketing applications. It has a Shore A Hardness reading of 89 and exhibits superior thermal stability, very low water absorption, robust tensile strength, tensile elongation, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Electronics

Display Devices

Automotive

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.03 [-] Show Supplier Material materials with Relative density of 1.03 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	210 % Show Supplier Material materials with Elongation of 210 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	0.1 GPa Show Supplier Material materials with Flexural modulus of 0.1 GPa	ISO 178 \| 12.5 mm/min
Hardness, Shore A	23.0 °C	89 [-] Show Supplier Material materials with Hardness, Shore A of 89 [-]	ASTM D 2240 \| 30S reading
Tensile strength	23.0 °C	18 MPa Show Supplier Material materials with Tensile strength of 18 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Value	Comment
Glow Wire Ignition Temperature	775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C	IEC 60695-2-13 \| 3.0 mm
Flammability	Glow Wire Flammability Index 960°C, passes at: 3mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3mm IEC 60695-2-12

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	600 V Show Supplier Material materials with Comparative tracking index of 600 V	IEC 60112 \|
Volume resistivity	23.0 °C	4.70E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 4.70E+15 Ω·cm	IEC 60093

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	17 g/10min Show Supplier Material materials with Melt mass-flow rate of 17 g/10min	ASTM D 1238 \| 250°C/10.0 kgf

Technological properties

Property
Application areas	Wireless Communications, Power Manangement, Heavy Vehicles, Wire & cable
Availability	Asia
Processing methods	Cooling Water Air Gap: 100 to 200.0mm Water Bath Temperature: 15 to 60.0°C Neck Temperature: 220 to 250.0°C Cross-head Temperature: 220 to 250.0°C Drying Temperature: 75 to 85.0°C Conductor Pre-heat Temperature: 25 to 120.0°C Drying Time: 5 to 7.0hrs Maximum Moisture Content: 0.02% Screw Speed: 15 to 85.0rpm Screen Pack: 150 to 100.0- Middle Zone Temperatures: 220 to 250.0°C Melt Temperature: 220 to 250.0°C Feed Zone Temperature: 180 to 220.0°C Die Temperature: 220 to 250.0°C Head Zone Temperature: 220 to 250.0°C Drying Time (Cumulative): 12hrs Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.