FLEX NORYL™ Resin WCD883CU - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCD883CU resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This UV stabilized material contains non-halogenated flame retardant and performance capable of meeting EN 50265-2-1 requirements. FLEX NORYL WCD883CU resin was developed for evaluation in AC cable jacket applications such as HD 21.14 flexible cables that require EU VDE and light color. It has a Shore A Hardness reading of 88 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

36 %

Show Supplier Material materials with Limiting oxygen index of 36 %

Relative density

23.0 °C

1.2 [-]

Show Supplier Material materials with Relative density of 1.2 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

135 %

Show Supplier Material materials with Elongation of 135 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

0.06 GPa

Show Supplier Material materials with Flexural modulus of 0.06 GPa

ISO 178 | 12.5 mm/min

Hardness, Shore A

23.0 °C

88 [-]

Show Supplier Material materials with Hardness, Shore A of 88 [-]

ASTM D 2240 | 30S reading

Tensile strength

23.0 °C

12.5 MPa

Show Supplier Material materials with Tensile strength of 12.5 MPa

ISO 527 | break, 50 mm/min

Thermal

PropertyValueComment

Brittleness temperature

-40 °C

Show Supplier Material materials with Brittleness temperature of -40 °C

<, ASTM D 746

Glow Wire Ignition Temperature

775 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C

IEC 60695-2-13 | 3.0 mm

Flammability

Glow Wire Flammability Index 960°C, passes at: 3mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3mm IEC 60695-2-12

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

IEC 60112 |

Dielectric constant, 1GHz

23.0 °C

3 [-]

Show Supplier Material materials with Dielectric constant, 1GHz of 3 [-]

SABIC method | 1.1 GHz

Dielectric strength

23.0 °C

25 kV/mm

Show Supplier Material materials with Dielectric strength of 25 kV/mm

IEC 60243-1 | in oil, 2.0mm

Dissipation factor, 1GHz

23.0 °C

3E-3 [-]

Show Supplier Material materials with Dissipation factor, 1GHz of 3E-3 [-]

SABIC method |

Sheet resistivity, ROA

23.0 °C

1.70E+16 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 1.70E+16 Ω

ASTM D 257

Volume resistivity

23.0 °C

1.20E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.20E+15 Ω·cm

ASTM D 257

Rheological Properties

PropertyValueComment

Melt mass-flow rate

10 g/10min

Show Supplier Material materials with Melt mass-flow rate of 10 g/10min

ASTM D 1238 | 250°C/10.0 kgf

Technological properties

Property
Application areas

Energy Management, Wiring Devices, Wire & cable

Availability

Asia

Features

Flexible, Hydrolytic Stability, Low Creep Sensitivity, Flame Retardant, Thin Wall, Non-Halogenated, Non-Chlorinated, Non-Brominated, Good Processability, Ductile

Processing methods

Drying Temperature: 75 to 85.0°C
Drying Time: 5 to 7.0hrs
Drying Time (Cumulative): 12hrs
Maximum Moisture Content: 0.02%
Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Screw Speed: 15 to 85.0rpm
Feed Zone Temperature: 180 to 220.0°C
Middle Zone Temperatures: 220 to 250.0°C
Head Zone Temperature: 220 to 250.0°C
Neck Temperature: 220 to 250.0°C
Cross-head Temperature: 220 to 250.0°C
Die Temperature: 220 to 250.0°C
Melt Temperature: 220 to 250.0°C
Conductor Pre-heat Temperature: 25 to 120.0°C
Screen Pack: 100 to 150.0-
Cooling Water Air Gap: 100 to 200.0mm
Water Bath Temperature: 15 to 60.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.