FLEX NORYL™ Resin WCD883AU - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCD883AU resin is a flexible, UV stabilized, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting EN 50265-2-1 requirements. FLEX NORYL WCD883AU resin is intended for evaluation in wire and cable applications such as HD 21.14 flexible cable jacketing. It has a Shore A Hardness reading of <87 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Limiting oxygen index	23.0 °C	36 % Show Supplier Material materials with Limiting oxygen index of 36 %
Relative density	23.0 °C	1.17 [-] Show Supplier Material materials with Relative density of 1.17 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.02 % Show Supplier Material materials with Water absorption of 0.02 %	ISO 62-1 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	235 % Show Supplier Material materials with Elongation of 235 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	0 GPa Show Supplier Material materials with Flexural modulus of 0 GPa	ISO 178 \| 12.5 mm/min
Hardness, Shore A	23.0 °C	87 [-] Show Supplier Material materials with Hardness, Shore A of 87 [-]	<, ASTM D 2240 \| 30S reading
Tensile strength	23.0 °C	15 MPa Show Supplier Material materials with Tensile strength of 15 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Value	Comment
Glow Wire Ignition Temperature	775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C	IEC 60695-2-13 \| 3.0 mm
Flammability	Smoke Density on 0.5mm plaque, Flame, Ds, max: 57- ASTM E 662 <br> Smoke Density on 0.5mm plaque, Non-flame, Ds, max: 142- ASTM E 662 <br> Glow Wire Flammability Index 850°C, passes at: 3mm IEC 60695-2-12

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	600 V Show Supplier Material materials with Comparative tracking index of 600 V	IEC 60112 \|
Dielectric constant, 1GHz	23.0 °C	3 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3 [-]	ASTM D 150
Dielectric strength	23.0 °C	25 kV/mm Show Supplier Material materials with Dielectric strength of 25 kV/mm	ASTM D 149 \| in oil
Dissipation factor, 1GHz	23.0 °C	3E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 3E-3 [-]	ASTM D 150
Sheet resistivity, ROA	23.0 °C	2.50E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 2.50E+16 Ω	ASTM D 257
Volume resistivity	23.0 °C	5.60E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 5.60E+15 Ω·cm	ASTM D 257

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	4 g/10min Show Supplier Material materials with Melt mass-flow rate of 4 g/10min	ASTM D 1238 \| 250°C/10.0 kgf

Technological properties

Property
Application areas	Wire & cable
Availability	Asia
Processing methods	Drying Time (Cumulative): 12hrs Screw Speed: 15 to 85.0rpm Conductor Pre-heat Temperature: 25 to 120.0°C Water Bath Temperature: 15 to 60.0°C Neck Temperature: 220 to 250.0°C Maximum Moisture Content: 0.02% Head Zone Temperature: 220 to 250.0°C Feed Zone Temperature: 180 to 220.0°C Middle Zone Temperatures: 220 to 250.0°C Die Temperature: 220 to 250.0°C Screen Pack: 150 to 100.0- Cross-head Temperature: 220 to 250.0°C Drying Temperature: 75 to 85.0°C Cooling Water Air Gap: 100 to 200.0mm Melt Temperature: 220 to 250.0°C Drying Time: 5 to 7.0hrs Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.