FLEX NORYL™ Resin WCD835 - Europe

Want to keep this datasheet? Save it now in your required format


FLEX NORYL™ WCD835 resin is a flexible, non-reinforced, low odor, migration improved, extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting UL VW-1 requirements, 80C end use temperature rating, and heat deformation performance as defined by UL 1581. FLEX NORYL WCD835 resin is intended for evaluation in wire insulation and cable jacket applications in dark colors. It has a Shore A Hardness reading of 83 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts




Relative density

23.0 °C

1.04 [-]

Show Supplier Material materials with Relative density of 1.04 [-]

ASTM D 792 |




23.0 °C

225 %

Show Supplier Material materials with Elongation of 225 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

0.03 GPa

Show Supplier Material materials with Flexural modulus of 0.03 GPa

ISO 178 | 12.5 mm/min

Hardness, Shore A

23.0 °C

83 [-]

Show Supplier Material materials with Hardness, Shore A of 83 [-]

ASTM D 2240 | 30S reading

Tensile strength

23.0 °C

10 MPa

Show Supplier Material materials with Tensile strength of 10 MPa

ISO 527 | break, 50 mm/min



Brittleness temperature

-40 °C

Show Supplier Material materials with Brittleness temperature of -40 °C

<, ASTM D 746

Glow Wire Ignition Temperature

750 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C

IEC 60695-2-13 | 3.0 mm


Glow Wire Flammability Index 850°C, passes at: 3mm IEC 60695-2-12



Comparative tracking index

23.0 °C

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

IEC 60112 |

Volume resistivity

23.0 °C

9.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 9.00E+15 Ω·cm

IEC 60093 |

Rheological Properties


Melt mass-flow rate

6 g/10min

Show Supplier Material materials with Melt mass-flow rate of 6 g/10min

ASTM D 1238 | 250°C/10.0 kgf

Technological properties

Application areas

Wire & cable




Flexible, Hydrolytic Stability, Low Creep Sensitivity, Flame Retardant, Thin Wall, Non-Halogenated, Non-Chlorinated, Non-Brominated, Good Processability, Ductile

Processing methods

Cooling Water Air Gap: 100 to 200.0mm
Maximum Moisture Content: 0.02%
Water Bath Temperature: 15 to 60.0°C
Screen Pack: 150 to 100.0-
Screw Speed: 15 to 85.0rpm
Melt Temperature: 220 to 250.0°C
Die Temperature: 220 to 250.0°C
Feed Zone Temperature: 180 to 220.0°C
Drying Time (Cumulative): 12hrs
Drying Temperature: 75 to 85.0°C
Middle Zone Temperatures: 220 to 250.0°C
Neck Temperature: 220 to 250.0°C
Cross-head Temperature: 220 to 250.0°C
Conductor Pre-heat Temperature: 25 to 120.0°C
Drying Time: 5 to 7.0hrs
Head Zone Temperature: 220 to 250.0°C
Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.