Description

XHT5141 is a high flow, high heat polycarbonate copolymer with a haze onset of 185C. It is available in a range of opaque colors.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Supplier Material materials with Density of 1.2 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.25 %

Show Supplier Material materials with Moisture absorption of 0.25 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.2 [-]

Show Supplier Material materials with Relative density of 1.2 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.5 %

Show Supplier Material materials with Water absorption of 0.5 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.5 GPa

Show Supplier Material materials with Elastic modulus of 2.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.55 GPa

Show Supplier Material materials with Flexural modulus of 2.55 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

120 MPa

Show Supplier Material materials with Flexural strength of 120 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²

ISO 180/1A | 80*10*3, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

80 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

65 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 65 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

80 MPa

Show Supplier Material materials with Tensile strength of 80 MPa

ISO 527 | yield, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*3, -30°C

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 165°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.5E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

183 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 183 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

170 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 170 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K)

ASTM C177 | @ 25 °C

Vicat softening temperature

190 °C

Show Supplier Material materials with Vicat softening temperature of 190 °C

ISO 306 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

16 g/10min

Show Supplier Material materials with Melt mass-flow rate of 16 g/10min

ASTM D 1238 | 330°C/2.16 kgf

Melt volume-flow rate

15 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 15 cm³/10min

ISO 1133 | MVR at 330°C/2.16kg

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Enclosures

Availability

Europe,Asia,Americas

Features

High Heat Resistance

Processing methods

Rear - Zone 1 Temperature: 300 to 325.0°C
Front - Zone 3 Temperature: 320 to 345.0°C
Back Pressure: 0.3 to 0.7MPa
Melt Temperature: 320 to 345.0°C
Maximum Moisture Content: 0.02%
Screw Speed: 40 to 70.0rpm
Drying Temperature: 135°C
Middle - Zone 2 Temperature: 310 to 335.0°C
Mold Temperature: 110 to 140.0°C
Nozzle Temperature: 315 to 340.0°C
Drying Time (Cumulative): 48hrs
Vent Depth: 0.025 to 0.08mm
Drying Time: 4 to 6.0hrs
Shot to Cylinder Size: 40 to 60.0%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.