LEXAN™ Copolymer XHT3143T - Americas

Want to keep this datasheet? Save it now in your required format

Description

XHT3143T is a high flow, UV stabilized, high heat polycarbonate copolymer. It is only available in limited transparent colors

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Supplier Material materials with Density of 1.2 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.3 %

Show Supplier Material materials with Moisture absorption of 0.3 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.21 [-]

Show Supplier Material materials with Relative density of 1.21 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.3 %

Show Supplier Material materials with Water absorption of 0.3 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.5 GPa

Show Supplier Material materials with Elastic modulus of 2.5 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.5 GPa

Show Supplier Material materials with Flexural modulus of 2.5 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

80 MPa

Show Supplier Material materials with Flexural strength of 80 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

9 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m²

ISO 180/1A | notched 80*10*3, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

97 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 97 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

68 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 68 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

70 MPa

Show Supplier Material materials with Tensile strength of 70 MPa

ISO 527 | yield, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*3, -30°C

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

152 - 166 °C

Show Supplier Material materials with Heat deflection temperature of 152 - 166 °C

Heat deflection temperature, 0.45 MPa

166 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 166 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

152 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 152 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

170 °C

Show Supplier Material materials with Vicat softening temperature of 170 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

33 g/10min

Show Supplier Material materials with Melt mass-flow rate of 33 g/10min

ASTM D 1238 | 330°C/2.16 kgf

Melt volume-flow rate

30 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 30 cm³/10min

ISO 1133 | MVR at 330°C/2.16kg

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Auto Aftermarket, Forward Lighting, Exterior, Electronic Components, Medical Device, Non-LED Lighting, Wireless Communications

Availability

Europe,Americas

Processing methods

Middle - Zone 2 Temperature: 280 to 310.0°C
Nozzle Temperature: 285 to 320.0°C
Drying Temperature: 135°C
Screw Speed: 40 to 90.0rpm
Back Pressure: 0.3 to 0.7MPa
Rear - Zone 1 Temperature: 270 to 300.0°C
Mold Temperature: 95 to 130.0°C
Maximum Moisture Content: 0.02%
Vent Depth: 0.025 to 0.08mm
Drying Time: 4 to 6.0hrs
Shot to Cylinder Size: 40 to 60.0%
Melt Temperature: 290 to 325.0°C
Front - Zone 3 Temperature: 290 to 325.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.