General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.25 % Show Supplier Material materials with Moisture absorption of 0.25 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.25 % Show Supplier Material materials with Water absorption of 0.25 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO 527 | yield, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 105 MPa Show Supplier Material materials with Flexural strength of 105 MPa | ISO 178 | yield, 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 145 MPa Show Supplier Material materials with Hardness, Ball Indentation of 145 MPa | ISO 2039-1 | H358/30 | ||
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Supplier Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 75 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 75 J/m | ASTM D 256 | notched, -30°C | ||
Tensile strength | 23.0 °C | 70 MPa Show Supplier Material materials with Tensile strength of 70 MPa | ISO 527 | yield, 50 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*3, -30°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | -30°C |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |
Coefficient of thermal expansion | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 138 - 150 °C Show Supplier Material materials with Heat deflection temperature of 138 - 150 °C | ||
Heat deflection temperature, 0.45 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 138 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 138 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K) | ASTM C177 | @ 25 °C |
Vicat softening temperature | 158 °C Show Supplier Material materials with Vicat softening temperature of 158 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 37 g/10min Show Supplier Material materials with Melt mass-flow rate of 37 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Melt volume-flow rate | 85 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 85 cm³/10min | ISO 1133 | MVR at 330°C/2.16kg | |
Shrinkage | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover | |
Availability | Europe,Asia,Americas | |
Processing methods | Back Pressure: 0.3 to 0.7MPa | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |