LEXAN™ Copolymer XHT1171 - Asia

Want to keep this datasheet? Save it now in your required format

Description

XHT1171 is an 85 MVR high flow, high heat polycarbonate copolymer enabling high aesthetics, thin wall and complex designs. It is available in a range of opaque colors.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Supplier Material materials with Density of 1.2 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.25 %

Show Supplier Material materials with Moisture absorption of 0.25 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.2 [-]

Show Supplier Material materials with Relative density of 1.2 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.25 %

Show Supplier Material materials with Water absorption of 0.25 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.4 GPa

Show Supplier Material materials with Elastic modulus of 2.4 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.35 GPa

Show Supplier Material materials with Flexural modulus of 2.35 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

105 MPa

Show Supplier Material materials with Flexural strength of 105 MPa

ISO 178 | yield, 2 mm/min

Hardness, Ball Indentation

23.0 °C

145 MPa

Show Supplier Material materials with Hardness, Ball Indentation of 145 MPa

ISO 2039-1 | H358/30

Hardness, Rockwell R

23.0 °C

125 [-]

Show Supplier Material materials with Hardness, Rockwell R of 125 [-]

ISO 2039-2

Impact strength, Charpy notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

9 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m²

ISO 180/1A | notched 80*10*3, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

75 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 75 J/m

ASTM D 256 | notched, -30°C

Tensile strength

23.0 °C

70 MPa

Show Supplier Material materials with Tensile strength of 70 MPa

ISO 527 | yield, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*3, 23°C,

Impact strength, Izod unnotched, ASTM

ASTM D 4812 | -30°C

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

150 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

138 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 138 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K)

ASTM C177 | @ 25 °C

Vicat softening temperature

158 °C

Show Supplier Material materials with Vicat softening temperature of 158 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

37 g/10min

Show Supplier Material materials with Melt mass-flow rate of 37 g/10min

ASTM D 1238 | 300°C/2.16 kgf

Melt volume-flow rate

85 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 85 cm³/10min

ISO 1133 | MVR at 330°C/2.16kg

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Enclosure/Housing/Cover

Availability

Europe,Asia,Americas

Features

High Heat Resistance

Processing methods

Maximum Moisture Content: 0.02%
Front - Zone 3 Temperature: 290 to 335.0°C
Back Pressure: 0.3 to 0.7MPa
Mold Temperature: 85 to 130.0°C
Drying Time: 4 to 6.0hrs
Rear - Zone 1 Temperature: 270 to 315.0°C
Middle - Zone 2 Temperature: 280 to 325.0°C
Drying Temperature: 130°C
Melt Temperature: 290 to 335.0°C
Shot to Cylinder Size: 40 to 60.0%
Nozzle Temperature: 285 to 330.0°C
Screw Speed: 40 to 90.0rpm
Vent Depth: 0.025 to 0.08mm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.