LEXAN™ Copolymer FST9405T - Americas

Want to keep this datasheet? Save it now in your required format

Description

Lexan* FST9405T resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.583 compliant and an ideal candidate foraircraft interior applications. Available in transparent and/or translucent colors only

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.33 g/cm³

Show Supplier Material materials with Density of 1.33 g/cm³

ISO 1183

Relative density

23.0 °C

1.33 [-]

Show Supplier Material materials with Relative density of 1.33 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.6 GPa

Show Supplier Material materials with Elastic modulus of 2.6 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

95 %

Show Supplier Material materials with Elongation of 95 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.5 GPa

Show Supplier Material materials with Flexural modulus of 2.5 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

105 MPa

Show Supplier Material materials with Flexural strength of 105 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m²

ISO 180/1A | 80*10*3, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

130 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 130 J/m

ASTM D 256 | notched, 23°C

Instrumented Impact, Total Energy

23.0 °C

60 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

70 MPa

Show Supplier Material materials with Tensile strength of 70 MPa

ISO 527 | break, 50 mm/min

Impact strength, Charpy notched

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*3, 23°C,

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

94 - 104 °C

Show Supplier Material materials with Heat deflection temperature of 94 - 104 °C

Heat deflection temperature, 0.45 MPa

104 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 104 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

94 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 94 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

113 °C

Show Supplier Material materials with Vicat softening temperature of 113 °C

ISO 306 | Rate B/120

Flammability

NBS Smoke Density, Flaming, Dmax: <75- ASTM E 662 <br> OSU peak heat release rate (5 minute test): <55kW/m² FAR 25.853 <br> Vertical Burn a (60s) passes at: 1sec FAR 25.853

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

9 g/10min

Show Supplier Material materials with Melt mass-flow rate of 9 g/10min

ASTM D 1238 | 300°C/1.2 kgf

Melt volume-flow rate

10 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min

ISO 1133 | MVR at 300°C/1.2 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method

Shrinkage, transverse

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage, transverse of 0.5 %

SABIC method

Technological properties

Property
Application areas

Air Cabin Interiors, Aircraft Seating

Availability

Europe,Asia,Americas

Processing methods

Mold Temperature: 50 to 80.0°C
Drying Temperature: 95 to 100.0°C
Rear - Zone 1 Temperature: 230 to 250.0°C
Drying Time: 6 to 8.0hrs
Middle - Zone 2 Temperature: 240 to 270.0°C
Nozzle Temperature: 245 to 275.0°C
Back Pressure: 0.3 to 0.7MPa
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 250 to 280.0°C
Screw Speed: 40 to 70.0rpm
Shot to Cylinder Size: 40 to 60.0%
Front - Zone 3 Temperature: 250 to 280.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.