General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.33 g/cm³ Show Supplier Material materials with Density of 1.33 g/cm³ | ISO 1183 |
Relative density | 23.0 °C | 1.33 [-] Show Supplier Material materials with Relative density of 1.33 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Elastic modulus of 2.6 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 6 % Show Supplier Material materials with Elongation of 6 % | ISO 527 | yield, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 105 MPa Show Supplier Material materials with Flexural strength of 105 MPa | ISO 178 | yield, 2 mm/min | ||
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 130 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 130 J/m | ASTM D 256 | notched, 23°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 70 MPa Show Supplier Material materials with Tensile strength of 70 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Charpy notched | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, 23°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*3, -30°C |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 94 - 104 °C Show Supplier Material materials with Heat deflection temperature of 94 - 104 °C | ||||
Heat deflection temperature, 0.45 MPa | 104 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 104 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 94 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 94 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Vicat softening temperature | 113 °C Show Supplier Material materials with Vicat softening temperature of 113 °C | ISO 306 | Rate B/120 | |||
Flammability | Vertical Burn a (60s) passes at: 1sec FAR 25.853 <br> OSU peak heat release rate (5 minute test): <55kW/m² FAR 25.853 <br> NBS Smoke Density, Flaming, Dmax: <75- ASTM E 662 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 9 g/10min Show Supplier Material materials with Melt mass-flow rate of 9 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 10 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Aircraft Seating, Air Cabin Interiors | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 6 to 8.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |