LEXAN™ Copolymer FST3403 - Europe

Want to keep this datasheet? Save it now in your required format

Description

LEXAN FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior applications (category R6). It also meets requirements of DIN5510-2, NFPA-130 and PN-K-02511 standards. Available in opaque colors.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.33 g/cm³

Show Supplier Material materials with Density of 1.33 g/cm³

ISO 1183

Relative density

23.0 °C

1.33 [-]

Show Supplier Material materials with Relative density of 1.33 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.6 GPa

Show Supplier Material materials with Elastic modulus of 2.6 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

80 %

Show Supplier Material materials with Elongation of 80 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.7 GPa

Show Supplier Material materials with Flexural modulus of 2.7 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

110 MPa

Show Supplier Material materials with Flexural strength of 110 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A | notched 80*10*3, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

90 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m

ASTM D 256 | notched, -30°C

Instrumented Impact, Total Energy

23.0 °C

80 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 80 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

77 MPa

Show Supplier Material materials with Tensile strength of 77 MPa

ISO 527 | yield, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | 80*10*3, 23°C

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

95 - 105 °C

Show Supplier Material materials with Heat deflection temperature of 95 - 105 °C

Heat deflection temperature, 0.45 MPa

105 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 105 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

95 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 95 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

115 °C

Show Supplier Material materials with Vicat softening temperature of 115 °C

ISO 306 | Rate B/120

Flammability

Smoke toxicity, CITG (8 min), 50 kW/m2, 3 mm: 0.1- ISO 5659-2 <br> Smoke density, VOF4, 50 kW/m2, 3mm: <300- ISO 5659-2 <br> Smoke density, DS-4, 50 kW/m2, 3mm: <150- ISO 5659-2 <br> Heat release, MAHRE, 50 kW/m2, 3 mm: <60kW/m² ISO 5660-1 <br> Fire Safety Hazard Level - Requirement set R6: HL3- EN 45545-2:2013

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

12 g/10min

Show Supplier Material materials with Melt mass-flow rate of 12 g/10min

ASTM D 1238 | 300°C/1.2 kgf

Melt volume-flow rate

10 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min

ISO 1133 | MVR at 300°C/1.2 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method

Shrinkage, transverse

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage, transverse of 0.5 %

SABIC method

Technological properties

Property
Application areas

Exterior Rail Components, Amusement Machine, Rail Seating, Rail Cabin Interiors, Interior Rail Components, Wireless Communications, Wiring Devices

Availability

Europe,Asia,Americas

Processing methods

Drying Time: 6 to 8.0hrs
Mold Temperature: 50 to 80.0°C
Back Pressure: 0.3 to 0.7MPa
Nozzle Temperature: 245 to 285.0°C
Drying Temperature: 95 to 100.0°C
Middle - Zone 2 Temperature: 240 to 280.0°C
Vent Depth: 0.025 to 0.076mm
Front - Zone 3 Temperature: 250 to 290.0°C
Screw Speed: 40 to 70.0rpm
Rear - Zone 1 Temperature: 230 to 260.0°C
Shot to Cylinder Size: 40 to 60.0%
Melt Temperature: 250 to 290.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.