LEXAN™ Copolymer FST3002 - Europe

Want to keep this datasheet? Save it now in your required format

Description

LEXAN FST3002 resin is a halogen-free flame retardant PC Copolymer Resin with MVR of 8, suitable for injection molding. This resin is EN45545 R6 HL2 compliant and an ideal candidate for train interior applications (category R6). Available in opaque colors

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Supplier Material materials with Density of 1.22 g/cm³

ISO 1183

Relative density

23.0 °C

1.22 [-]

Show Supplier Material materials with Relative density of 1.22 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.45 GPa

Show Supplier Material materials with Elastic modulus of 2.45 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.4 GPa

Show Supplier Material materials with Flexural modulus of 2.4 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

107 MPa

Show Supplier Material materials with Flexural strength of 107 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

9 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A | 80*10*3, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

60 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m

ASTM D 256

Instrumented Impact, Total Energy

23.0 °C

70 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 70 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

74 MPa

Show Supplier Material materials with Tensile strength of 74 MPa

ISO 527 | yield, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*4

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature

111 - 125 °C

Show Supplier Material materials with Heat deflection temperature of 111 - 125 °C

Heat deflection temperature, 0.45 MPa

125 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 125 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

111 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 111 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

130 °C

Show Supplier Material materials with Vicat softening temperature of 130 °C

ISO 306 | Rate B/50

Flammability

Smoke density, VOF4, 50 kW/m2, 3mm: <600- ISO 5659-2 <br> Smoke density, DS-4, 50 kW/m2, 3mm: <300- ISO 5659-2 <br> Heat release, MAHRE, 50 kW/m2, 3 mm: <90kW/m² ISO 5660-1 <br> Smoke toxicity, CITG (8 min), 50 kW/m2, 3 mm: <0.9- ISO 5659-2 <br> Fire Safety Hazard Level - Requirement set R6: HL2- EN 45545-2:2013

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

9 g/10min

Show Supplier Material materials with Melt mass-flow rate of 9 g/10min

ASTM D 1238 | 300°C/1.2 kgf

Melt volume-flow rate

8 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 8 cm³/10min

ISO 1133 | MVR at 300°C/1.2 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method

Shrinkage, transverse

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage, transverse of 0.5 %

SABIC method

Technological properties

Property
Application areas

Rail Cabin Interiors, Rail Seating, Enclosures

Availability

Europe

Features

Low Smoke and Toxicity

Processing methods

Hopper Temperature: 60 to 80.0°C
Nozzle Temperature: 270 to 290.0°C
Melt Temperature: 280 to 300.0°C
Drying Temperature: 120°C
Drying Time: 2 to 4.0hrs
Rear - Zone 1 Temperature: 260 to 280.0°C
Mold Temperature: 80 to 100.0°C
Front - Zone 3 Temperature: 280 to 300.0°C
Middle - Zone 2 Temperature: 270 to 290.0°C
Maximum Moisture Content: 0.02%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.