LEXAN™ Copolymer EXL1414H - Europe

Want to keep this datasheet? Save it now in your required format

Description

Opaque PC-Siloxan copolymer with excellent processability. Medium flow, extreme low temperature ductile. Enhanced hydrolytic stability. Only available in black color.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Supplier Material materials with Density of 1.19 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.15 %

Show Supplier Material materials with Moisture absorption of 0.15 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.18 [-]

Show Supplier Material materials with Relative density of 1.18 [-]

ASTM D 792 |

Water absorption

23.0 °C

0.35 %

Show Supplier Material materials with Water absorption of 0.35 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.15 GPa

Show Supplier Material materials with Elastic modulus of 2.15 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.25 GPa

Show Supplier Material materials with Flexural modulus of 2.25 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

85 MPa

Show Supplier Material materials with Flexural strength of 85 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

65 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 65 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C

Impact strength, Izod notched

23.0 °C

70 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 70 kJ/m²

ISO 180/1A | 80*10*3, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

865 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 865 J/m

ASTM D 256 | notched, 23°C

Instrumented Impact, Total Energy

23.0 °C

77 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 77 J

ASTM D 3763 | -30°C

Tensile strength

23.0 °C

60 MPa

Show Supplier Material materials with Tensile strength of 60 MPa

ISO 527 | break, 50 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, 23°C

Impact strength, Izod unnotched

ISO 180/1U | 80*10*3, 23°C

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

nan

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

7.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7.2E-5 1/K

ISO 11359-2 | 23°C to 80°C

Coefficient of thermal expansion, transverse

23.0 °C

7.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K

ISO 11359-2 | 23°C to 80°C

Heat deflection temperature, 0.45 MPa

140 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 140 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

128 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 128 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Vicat softening temperature

145 °C

Show Supplier Material materials with Vicat softening temperature of 145 °C

ISO 306 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

10 g/10min

Show Supplier Material materials with Melt mass-flow rate of 10 g/10min

ASTM D 1238 | 300°C/1.2 kgf

Melt volume-flow rate

9 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 9 cm³/10min

ISO 1133 | MVR at 300°C/1.2 kg

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Enclosures

Availability

Europe,Asia,Americas

Features

High Impact Resistance

Processing methods

Back Pressure: 0.3 to 0.7MPa
Maximum Moisture Content: 0.02%
Shot to Cylinder Size: 40 to 60.0%
Drying Time (Cumulative): 48hrs
Front - Zone 3 Temperature: 295 to 315.0°C
Drying Temperature: 120°C
Rear - Zone 1 Temperature: 270 to 295.0°C
Drying Time: 3 to 4.0hrs
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 295 to 315.0°C
Mold Temperature: 70 to 95.0°C
Middle - Zone 2 Temperature: 280 to 305.0°C
Nozzle Temperature: 290 to 310.0°C
Screw Speed: 40 to 70.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.