LNP™ THERMOCOMP™ Compound QF007 - Asia

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.33 g/cm³

Show Supplier Material materials with Density of 1.33 g/cm³

ASTM D 792

Moisture absorption

23.0 °C

0.2 %

Show Supplier Material materials with Moisture absorption of 0.2 %

ASTM D 570 | (23°C/50% RH/24 hrs)

Mechanical

PropertyTemperatureValueComment

Flexural modulus

23.0 °C

8.9 GPa

Show Supplier Material materials with Flexural modulus of 8.9 GPa

ASTM D 790

Flexural strength

23.0 °C

268 MPa

Show Supplier Material materials with Flexural strength of 268 MPa

ASTM D 790

Impact strength, Izod notched

23.0 °C

130 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 130 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

130 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 130 J/m

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

176 MPa

Show Supplier Material materials with Tensile strength of 176 MPa

ASTM D 638 | break

Technological properties

Property
Availability

Asia,Americas

Processing methods

Front - Zone 3 Temperature: 270 to 280.0°C
Back Pressure: 0.2 to 0.3MPa
Mold Temperature: 80 to 95.0°C
Maximum Moisture Content: 0.12 to 0.2%
Middle - Zone 2 Temperature: 260 to 270.0°C
Drying Time: 4hrs
Screw Speed: 30 to 60.0rpm
Melt Temperature: 270 to 275.0°C
Drying Temperature: 80°C
Rear - Zone 1 Temperature: 250 to 260.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.