LNP™ THERMOCOMP™ Compound ZF006 - Asia

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP ZF006 is a compound based on PPO resin containing 30% Glass Fiber.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.31 g/cm³

Show Supplier Material materials with Density of 1.31 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Flexural modulus

23.0 °C

8.6 GPa

Show Supplier Material materials with Flexural modulus of 8.6 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ASTM D 790

Impact strength, Izod notched

23.0 °C

114 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 114 kJ/m²

ASTM D 256 | notched, 23°C

Thermal

PropertyValueComment

Heat deflection temperature

135 °C

Show Supplier Material materials with Heat deflection temperature of 135 °C

Heat deflection temperature, 1.80 MPa

135 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 135 °C

ASTM D 648 | 3.2mm, unannealed

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

ASTM D 955 | 24 hrs

Technological properties

Property
Availability

Europe,Asia,Americas

Processing methods

Drying Time: 4hrs
Middle - Zone 2 Temperature: 290 to 300.0°C
Screw Speed: 30 to 60.0rpm
Back Pressure: 0.2 to 0.3MPa
Front - Zone 3 Temperature: 300 to 310.0°C
Mold Temperature: 80 to 110.0°C
Drying Temperature: 120°C
Rear - Zone 1 Temperature: 275 to 290.0°C
Melt Temperature: 300 to 305.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.