LNP™ THERMOCOMP™ Compound ZF006 - Europe

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP ZF006 is a compound based on PPO resin containing 30% Glass Fiber.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.33 g/cm³

Show Supplier Material materials with Density of 1.33 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Flexural modulus

23.0 °C

6.9 GPa

Show Supplier Material materials with Flexural modulus of 6.9 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

138 MPa

Show Supplier Material materials with Flexural strength of 138 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

132 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 132 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.23 %

Show Supplier Material materials with Shrinkage of 0.23 %

SABIC method

Technological properties

Property
Availability

Europe,Asia,Americas

Features

High Stiffness, Structural

Processing methods

Melt Temperature: 300 to 305.0°C
Back Pressure: 0.2 to 0.3MPa
Rear - Zone 1 Temperature: 275 to 290.0°C
Mold Temperature: 80 to 110.0°C
Drying Time: 4hrs
Front - Zone 3 Temperature: 300 to 310.0°C
Screw Speed: 30 to 60.0rpm
Middle - Zone 2 Temperature: 290 to 300.0°C
Drying Temperature: 120°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.