LNP™ LUBRICOMP™ Compound YL003 - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP* LUBRICOMP* YL003 is a compound based on Polyester Elastomer resin containing 15% PTFE. Added feature of this grade is: Wear Resistant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.18 GPa

Show Supplier Material materials with Elastic modulus of 0.18 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

455 %

Show Supplier Material materials with Elongation of 455 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

0.23 GPa

Show Supplier Material materials with Flexural modulus of 0.23 GPa

ISO 178 | 2 mm/min

Impact strength, Izod notched

23.0 °C

21 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 21 kJ/m²

ISO 180/1A | notched 80*10*4, 23°C

Tensile strength

23.0 °C

24 MPa

Show Supplier Material materials with Tensile strength of 24 MPa

ISO 527 | yield, 50 mm/min

Impact strength, Izod unnotched

ISO 180/1U | 80*10*4, 23°C

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1 %

Show Supplier Material materials with Shrinkage of 1 %

ASTM D 955 | 24 hrs

Shrinkage, transverse

23.0 °C

1 %

Show Supplier Material materials with Shrinkage, transverse of 1 %

ASTM D 955 | 24 hrs

Technological properties

Property
Availability

Europe,Americas

Features

Wear resistant, Wear and Friction

Processing methods

Drying Temperature: 80°C
Maximum Moisture Content: 0.1%
Drying Time: 4hrs
Mold Temperature: 25 to 55.0°C
Back Pressure: 0.2 to 0.3MPa
Melt Temperature: 215 to 240.0°C
Front - Zone 3 Temperature: 225 to 240.0°C
Middle - Zone 2 Temperature: 205 to 215.0°C
Screw Speed: 30 to 60.0rpm
Rear - Zone 1 Temperature: 180 to 195.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.