General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.59 g/cm³ Show Supplier Material materials with Density of 1.59 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.5 GPa Show Supplier Material materials with Elastic modulus of 8.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.7 % Show Supplier Material materials with Elongation of 2.7 % | ISO 527 | yield, 50 mm/min |
Flexural modulus | 23.0 °C | 7.5 GPa Show Supplier Material materials with Flexural modulus of 7.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 182 MPa Show Supplier Material materials with Flexural strength of 182 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 86 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 86 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 780 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 780 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 121 MPa Show Supplier Material materials with Tensile strength of 121 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Technological properties
Property | ||
---|---|---|
Application areas | Pharmaceutical Packaging & Drug Delivery | |
Availability | Europe,Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |