LNP™ LUBRICOMP™ Compound WBL36L - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Coefficient of friction		0.63 - 0.66 [-] Show Supplier Material materials with Coefficient of friction of 0.63 - 0.66 [-]
Coefficient of friction, kinetic		0.66 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.66 [-]	ASTM D 3702 Modified: Manual
Coefficient of friction, static		0.63 [-] Show Supplier Material materials with Coefficient of friction, static of 0.63 [-]	ASTM D 3702 Modified: Manual
Density	23.0 °C	1.69 g/cm³ Show Supplier Material materials with Density of 1.69 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	4 GPa Show Supplier Material materials with Elastic modulus of 4 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2.4 % Show Supplier Material materials with Elongation of 2.4 %	ISO 527 \| yield, 5 mm/min
Flexural modulus	23.0 °C	3.9 GPa Show Supplier Material materials with Flexural modulus of 3.9 GPa	ISO 178
Flexural strength	23.0 °C	75 MPa Show Supplier Material materials with Flexural strength of 75 MPa	ISO 178
Impact strength, Izod notched	23.0 °C	3 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 3 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	32 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 32 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched	23.0 °C	18 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 18 kJ/m²	ISO 180/1U \| unnotched 80104
Impact strength, Izod unnotched, ASTM	23.0 °C	256 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 256 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, at Peak	23.0 °C	3 J Show Supplier Material materials with Instrumented Impact, at Peak of 3 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	37 MPa Show Supplier Material materials with Tensile strength of 37 MPa	ISO 527 \| yield, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	7.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.4E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Coefficient of thermal expansion, transverse	23.0 °C	7.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.1E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Heat deflection temperature		94 - 184 °C Show Supplier Material materials with Heat deflection temperature of 94 - 184 °C
Heat deflection temperature, 0.45 MPa		184 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 184 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		94 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 94 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	2.4 % Show Supplier Material materials with Shrinkage of 2.4 %	ISO 294 \| 24 hrs
Shrinkage, transverse	23.0 °C	1.9 % Show Supplier Material materials with Shrinkage, transverse of 1.9 %	ISO 294 \| 24 hrs

Technological properties

Property
Application areas	Enclosures
Availability	Asia,Americas
Processing methods	Screw Speed: 30 to 60.0rpm Maximum Moisture Content: 0.05% Melt Temperature: 240 to 265.0°C Mold Temperature: 80 to 100.0°C Middle - Zone 2 Temperature: 245 to 255.0°C Back Pressure: 0.2 to 0.3MPa Drying Time: 4hrs Rear - Zone 1 Temperature: 220 to 230.0°C Drying Temperature: 120°C Front - Zone 3 Temperature: 260 to 270.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.