LNP™ LUBRICOMP™ Compound WBL36L - Asia

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Coefficient of friction

0.63 - 0.66 [-]

Show Supplier Material materials with Coefficient of friction of 0.63 - 0.66 [-]

Coefficient of friction, kinetic

0.66 [-]

Show Supplier Material materials with Coefficient of friction, kinetic of 0.66 [-]

ASTM D 3702 Modified: Manual

Coefficient of friction, static

0.63 [-]

Show Supplier Material materials with Coefficient of friction, static of 0.63 [-]

ASTM D 3702 Modified: Manual

Density

23.0 °C

1.69 g/cm³

Show Supplier Material materials with Density of 1.69 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.02 GPa

Show Supplier Material materials with Elastic modulus of 4.02 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

3.3 %

Show Supplier Material materials with Elongation of 3.3 %

ISO 527 | break

Flexural modulus

23.0 °C

4.14 GPa

Show Supplier Material materials with Flexural modulus of 4.14 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

75 MPa

Show Supplier Material materials with Flexural strength of 75 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

3 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 3 kJ/m²

ISO 180/1A | notched 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

32 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 32 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched

23.0 °C

18 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 18 kJ/m²

ISO 180/1U | unnotched 80*10*4, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

256 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 256 J/m

ASTM D 4812 | 23°C

Instrumented Impact, at Peak

23.0 °C

3 J

Show Supplier Material materials with Instrumented Impact, at Peak of 3 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

36 MPa

Show Supplier Material materials with Tensile strength of 36 MPa

ISO 527 | break

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.4E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 7.4E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7.1E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.1E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

94 - 184 °C

Show Supplier Material materials with Heat deflection temperature of 94 - 184 °C

Heat deflection temperature, 0.45 MPa

184 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 184 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

94 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 94 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

2.4 %

Show Supplier Material materials with Shrinkage of 2.4 %

SABIC method

Shrinkage, transverse

23.0 °C

1.9 %

Show Supplier Material materials with Shrinkage, transverse of 1.9 %

SABIC method

Technological properties

Property
Application areas

Enclosures

Availability

Asia,Americas

Features

Good dimensional stability, Wear resistant, Low Warpage, Wear and Friction

Processing methods

Front - Zone 3 Temperature: 250 to 260.0°C
Middle - Zone 2 Temperature: 240 to 250.0°C
Mold Temperature: 80 to 100.0°C
Maximum Moisture Content: 0.05%
Drying Temperature: 120°C
Screw Speed: 30 to 60.0rpm
Back Pressure: 0.2 to 0.3MPa
Rear - Zone 1 Temperature: 220 to 230.0°C
Melt Temperature: 240 to 250.0°C
Drying Time: 4hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.