LNP™ LUBRICOMP™ Compound RL002 - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing 10% PTFE. Added features of this material include: Wear Resistant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Supplier Material materials with Density of 1.19 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3 GPa

Show Supplier Material materials with Elastic modulus of 3 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

4.5 %

Show Supplier Material materials with Elongation of 4.5 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

2.6 GPa

Show Supplier Material materials with Flexural modulus of 2.6 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

95 MPa

Show Supplier Material materials with Flexural strength of 95 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | notched 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

55 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 55 kJ/m²

ISO 180/1U | unnotched 80*10*4, 23°C

Tensile strength

23.0 °C

74 MPa

Show Supplier Material materials with Tensile strength of 74 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

74 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 74 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

2.23 %

Show Supplier Material materials with Shrinkage of 2.23 %

ISO 294 | 24 hrs

Technological properties

Property
Application areas

Toy, Refrigerator, Monitoring and Imaging, Medical Device

Availability

Europe,Americas

Features

Wear and Friction

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.