LNP™ STAT-KON™ Compound RE006 - Asia

Want to keep this datasheet? Save it now in your required format

Description

LNP STAT-KON* RE006 is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

2.3 %

Show Supplier Material materials with Elongation of 2.3 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

17 GPa

Show Supplier Material materials with Flexural modulus of 17 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

355 MPa

Show Supplier Material materials with Flexural strength of 355 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

119 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 119 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

1030 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1030 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

238 MPa

Show Supplier Material materials with Tensile strength of 238 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

248 °C

Show Supplier Material materials with Heat deflection temperature of 248 °C

Heat deflection temperature, 1.80 MPa

248 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 248 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Electrical

PropertyTemperatureValueComment

Sheet resistivity, ROA

23.0 °C

100 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 100 Ω

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.1 %

Show Supplier Material materials with Shrinkage of 0.1 %

ASTM D 955 | 24 hrs

Shrinkage, transverse

23.0 °C

1 %

Show Supplier Material materials with Shrinkage, transverse of 1 %

ASTM D 955 | 24 hrs

Technological properties

Property
Availability

Asia,Americas

Processing methods

Screw Speed: 30 to 60.0rpm
Maximum Moisture Content: 0.15 to 0.25%
Rear - Zone 1 Temperature: 265 to 275.0°C
Back Pressure: 0.2 to 0.3MPa
Front - Zone 3 Temperature: 295 to 305.0°C
Middle - Zone 2 Temperature: 280 to 295.0°C
Mold Temperature: 95 to 110.0°C
Drying Time: 4hrs
Melt Temperature: 280 to 305.0°C
Drying Temperature: 80°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.