LNP™ STAT-KON™ Compound RE003 - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP STAT-KON* RE003 is a compound based on Nylon 66 resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Supplier Material materials with Density of 1.2 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11.2 GPa

Show Supplier Material materials with Elastic modulus of 11.2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

10.7 GPa

Show Supplier Material materials with Flexural modulus of 10.7 GPa

ISO 178

Flexural strength

23.0 °C

237 MPa

Show Supplier Material materials with Flexural strength of 237 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

35 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 35 kJ/m²

ISO 180/1U | unnotched 80*10*4, 23°C

Tensile strength

23.0 °C

180 MPa

Show Supplier Material materials with Tensile strength of 180 MPa

ISO 527 | break

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.43E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.43E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.86E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.86E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature

245 - 260 °C

Show Supplier Material materials with Heat deflection temperature of 245 - 260 °C

Heat deflection temperature, 0.45 MPa

260 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 260 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

245 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 245 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Electrical

PropertyTemperatureValueComment

Sheet resistivity, ROA

23.0 °C

100 - 1000000 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 100 - 1000000 Ω

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.17 %

Show Supplier Material materials with Shrinkage of 0.17 %

ISO 294 | 24 hrs

Technological properties

Property
Availability

Europe,Americas

Processing methods

Rear - Zone 1 Temperature: 265 to 275.0°C
Maximum Moisture Content: 0.15 to 0.25%
Back Pressure: 0.2 to 0.3MPa
Front - Zone 3 Temperature: 295 to 305.0°C
Screw Speed: 30 to 60.0rpm
Mold Temperature: 95 to 110.0°C
Drying Temperature: 80°C
Melt Temperature: 280 to 305.0°C
Drying Time: 4hrs
Middle - Zone 2 Temperature: 280 to 295.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.