LNP™ LUBRICOMP™ Compound RAL22 - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Coefficient of friction

0.45 - 0.54 [-]

Show Supplier Material materials with Coefficient of friction of 0.45 - 0.54 [-]

Coefficient of friction, kinetic

0.54 [-]

Show Supplier Material materials with Coefficient of friction, kinetic of 0.54 [-]

ASTM D 3702 Modified: Manual

Coefficient of friction, static

0.45 [-]

Show Supplier Material materials with Coefficient of friction, static of 0.45 [-]

ASTM D 3702 Modified: Manual

Density

23.0 °C

1.22 g/cm³

Show Supplier Material materials with Density of 1.22 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.6 GPa

Show Supplier Material materials with Elastic modulus of 3.6 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

9.5 %

Show Supplier Material materials with Elongation of 9.5 %

ISO 527 | break

Flexural modulus

23.0 °C

3.5 GPa

Show Supplier Material materials with Flexural modulus of 3.5 GPa

ISO 178

Flexural strength

23.0 °C

106 MPa

Show Supplier Material materials with Flexural strength of 106 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | notched 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

48 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 48 kJ/m²

ISO 180/1U | unnotched 80*10*4, 23°C

Tensile strength

23.0 °C

79 MPa

Show Supplier Material materials with Tensile strength of 79 MPa

ISO 527 | break

Thermal

PropertyValueComment

Heat deflection temperature

193 °C

Show Supplier Material materials with Heat deflection temperature of 193 °C

Heat deflection temperature, 1.80 MPa

193 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 193 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.92 %

Show Supplier Material materials with Shrinkage of 1.92 %

ISO 294 | 24 hrs

Technological properties

Property
Application areas

ATM/Ticket Machine, Document Handling, Electronic Components, Gear/Bearing/Slider

Availability

Europe,Asia,Americas

Processing methods

Melt Temperature: 275 to 290.0°C
Front - Zone 3 Temperature: 295 to 305.0°C
Drying Time: 4hrs
Middle - Zone 2 Temperature: 280 to 295.0°C
Maximum Moisture Content: 0.15 to 0.25%
Rear - Zone 1 Temperature: 265 to 275.0°C
Mold Temperature: 80 to 95.0°C
Drying Temperature: 80°C
Screw Speed: 30 to 60.0rpm
Back Pressure: 0.2 to 0.3MPa

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.