LNP™ THERMOCOMP™ Compound QC006 - Americas

Want to keep this datasheet? Save it now in your required format


LNP THERMOCOMP* QC006 is a compound based on Nylon 6/10 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts





23.0 °C

1.24 g/cm³

Show Supplier Material materials with Density of 1.24 g/cm³

ASTM D 792



Flexural modulus

23.0 °C

18.77 GPa

Show Supplier Material materials with Flexural modulus of 18.77 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

349 MPa

Show Supplier Material materials with Flexural strength of 349 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Tensile strength

23.0 °C

196 MPa

Show Supplier Material materials with Tensile strength of 196 MPa

ISO 527 | break, 5 mm/min



Heat deflection temperature, 1.80 MPa

205 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Technological properties




Low Moisture Absorption, Light-weight Structural, Super Strong (Carbon Fiber Filled), Electrostatic discharge, Electrically Conductive, Structural

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.