LNP™ LUBRICOMP™ Compound PFL38S - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP PFL38S is a compound based on Nylon 6 resin containing 40% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

10.34 GPa

Show Supplier Material materials with Flexural modulus of 10.34 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

220 MPa

Show Supplier Material materials with Flexural strength of 220 MPa

ASTM D 790 | brk, 1.3 mm/min, 50 mm span

Impact strength, Izod notched

23.0 °C

133 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 133 kJ/m²

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

152 MPa

Show Supplier Material materials with Tensile strength of 152 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature

212 °C

Show Supplier Material materials with Heat deflection temperature of 212 °C

Heat deflection temperature, 1.80 MPa

212 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 212 °C

ASTM D 648 | 3.2mm, unannealed

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

SABIC method | 48 hrs @ 23°C

Technological properties

Property
Availability

Europe,Americas

Features

Wear resistant, Heat Stabilized, Structural, Wear and Friction

Processing methods

Melt Temperature: 265 to 275.0°C
Drying Time: 4hrs
Maximum Moisture Content: 0.15 to 0.25%
Middle - Zone 2 Temperature: 265 to 275.0°C
Front - Zone 3 Temperature: 275 to 290.0°C
Rear - Zone 1 Temperature: 250 to 260.0°C
Back Pressure: 0.3 to 0.7MPa
Mold Temperature: 80 to 95.0°C
Screw Speed: 30 to 60.0rpm
Drying Temperature: 80°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.