LNP™ LUBRICOMP™ Compound PFL38S - Europe

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP PFL38S is a compound based on Nylon 6 resin containing 40% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	3.5 % Show Supplier Material materials with Elongation of 3.5 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	11.6 GPa Show Supplier Material materials with Flexural modulus of 11.6 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	251 MPa Show Supplier Material materials with Flexural strength of 251 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Izod notched	23.0 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 14 kJ/m²	ISO 180/1A \| 80104, 23°C
Tensile strength	23.0 °C	172 MPa Show Supplier Material materials with Tensile strength of 172 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	203 °C Show Supplier Material materials with Heat deflection temperature of 203 °C
Heat deflection temperature, 1.80 MPa	203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method

Technological properties

Property
Availability	Europe,Americas
Processing methods	Melt Temperature: 265 to 275.0°C Front - Zone 3 Temperature: 275 to 290.0°C Rear - Zone 1 Temperature: 250 to 260.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 30 to 60.0rpm Mold Temperature: 80 to 95.0°C Maximum Moisture Content: 0.15 to 0.25% Middle - Zone 2 Temperature: 265 to 275.0°C Drying Time: 4hrs Drying Temperature: 80°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.