LNP™ THERMOCOMP™ Compound LF006E - Americas

Want to keep this datasheet? Save it now in your required format


LNP THERMOCOMP LF006E is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

1.53 g/cm³

Show Supplier Material materials with Density of 1.53 g/cm³

ISO 1183



Elastic modulus

23.0 °C

12.9 GPa

Show Supplier Material materials with Elastic modulus of 12.9 GPa

ISO 527 | 1 mm/min


23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527 | break

Flexural modulus

23.0 °C

12.5 GPa

Show Supplier Material materials with Flexural modulus of 12.5 GPa

ISO 178

Flexural strength

23.0 °C

278 MPa

Show Supplier Material materials with Flexural strength of 278 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

58 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 58 kJ/m²

ISO 180/1U | 80*10*4, 23°C

Tensile strength

23.0 °C

187 MPa

Show Supplier Material materials with Tensile strength of 187 MPa

ISO 527 | break

Technological properties

Application areas

Electronic Components, Enclosures, Heavy Vehicles, Air Cabin Interiors, Oil/Gas



Processing methods

Front - Zone 3 Temperature: 380 to 400.0°C
Back Pressure: 0.3 to 0.7MPa
Middle - Zone 2 Temperature: 380 to 400.0°C
Screw Speed: 60 to 100.0rpm
Drying Time: 4 to 6.0hrs
Drying Temperature: 150°C
Rear - Zone 1 Temperature: 370 to 380.0°C
Mold Temperature: 175 to 190.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.